Method for producing glass plate, and laminate
A method for producing an intermediate glass plate includes a defect formation step, a separation step, and a polishing step. In the defect formation step, a defect is formed on main surfaces of glass blanks by irradiating a laminate of the glass blanks with a laser beam from one side in a lamination direction in which the glass blanks are laminated, along the lamination direction, and moving the laser beam relative to the laminate such that a circle is drawn in a view from the main surfaces of the glass blanks. In the separation step, a cylindrical laminate is formed by separating a removal target portion along the defect while maintaining the laminate. In the polishing step, a side wall surface of the laminate is polished while maintaining the cylindrical laminate so as to obtain a disk-shaped intermediate glass plate that has been subjected to edge surface polishing.
1 . A laminate comprising:
a plurality of circular glass plates; and
space holding members each of which is disposed between adjacent circular glass plates among the plurality of circular glass plates, such that the plurality of circular glass plates are laminated with a space interposed between the adjacent circular glass plates, wherein
the laminate has a cylindrical shape,
a cylindricity of an outer side wall surface of the cylindrical shape of the laminate is 7 μm or less, and
a plurality of defects that extend in a plate thickness direction are formed at positions on an edge surface of each of the plurality of circular glass plates, such that the positions are same among the plurality of circular glass plates as viewed the plate thickness direction.
2 . The laminate according to claim 1 , wherein
the plurality of defects are formed on the edge surface at an interval.
3 . The laminate according to claim 2 , wherein
the interval is 0.5 to 30 μm.
4 . The laminate according to claim 1 , wherein
the laminate has an inner hole, and a cylindricity of an inner side wall surface defined by the inner hole is 7 μm or less.
5 . The laminate according to claim 4 , wherein
a deviation between a central axis of the inner hole and a central axis of the cylindrical shape is 3 μm or less.
6 . A method for producing the laminate according to claim 1 , the method comprising:
forming a plurality of defects on main surfaces of a plurality of laminated glass blanks which are obtained by laminating glass blanks such that each of the space holding members is disposed between adjacent glass blanks among the glass blanks, by irradiating the laminated glass blanks, with a laser beam from one side in a lamination direction in which the glass blanks are laminated, along the lamination direction, and by moving the laser beam relative to the laminated glass blanks such that a circle is drawn in a view from the main surfaces of the glass blanks; and
separating a removal target portion along the defects while maintaining the laminating of the glass blanks to obtain the laminate.
7 . The method for producing the laminate according to claim 6 ,
wherein the outer side wall surface of the cylindrical shape of the laminate has an arithmetic average roughness Ra of 0.5 μm or less.
8 . The method for producing the laminate according to claim 6 ,
wherein the volume of the removal target portion is 35% or less of the total volume of the laminated glass blanks.
9 . The method for producing the laminate according to claim 6 ,
wherein, when the removal target portion is separated from the laminated glass blanks, the removal target portion is separated by advancing the defects by supplying an etchant to the laminated glass blanks.
10 . The method for producing the laminate according to claim 6 ,
wherein, when the removal target portion is separated from the laminated glass blanks, the removal target portion is separated by advancing the defects by applying heat to the laminated glass blanks.
11 . A method for producing a disk-shaped glass plate from a glass blank, the method comprising:
the method for producing the laminate according to claim 6 ; and
polishing the outer side wall surface of the laminate so as to obtain a disk-shaped glass plate that has been subjected to edge surface polishing.
12 . The method for producing a glass plate according to claim 6 ,
wherein, in the polishing the outer side wall surface, the polishing is performed so as to form a chamfered surface on each edge surface of the circular glass plate.
13 . The method for producing a glass plate according to claim 11 ,
wherein the glass plate is provided with an inner hole so as to have a circular inner circumference,
in the forming of the defects, the defects are formed in two circles in order to form a circular shape of an outer circumference and a circular shape of the inner circumference,
in the separating of the removal target portion, an outer portion of a larger circle of the two circles and an inner portion of a smaller circle of the two circles are removed from the laminated glass blanks as the removal target portions, and
in the polishing of the side wall surface of the laminate, side wall surfaces of the laminate that respectively correspond to the outer circumference and the inner circumference are polished.
14 . The method for producing a glass plate according to claim 11 , further comprising
polishing main surfaces of the glass plate that is separated from the laminate after the side wall surface is polished.