Reinforcing fiber mat, and fiber-reinforced resin forming material and method of producing same
A reinforcing fiber mat includes reinforcing fiber bundles having an average fiber length of 5 mm to 100 mm, wherein reinforcing fiber bundles consisting of 86 or more fibers per bundle are contained at a weight content of more than 99 wt % to 100 wt % and the reinforcing fiber bundles contain single yarns by 500 fibers/mm-width or more and 1,600 fibers/mm-width or less and have a drape level of 120 mm or more and 240 mm or less.
1. A reinforcing fiber mat comprising reinforcing fiber bundles having an average fiber length of 5 mm to 100 mm,
wherein reinforcing fiber bundles consisting of 86 or more fibers per bundle are contained at a weight content of more than 99 wt % to 100 wt %, and
the reinforcing fiber bundles contain single yarns by 500 fibers/mm-width or more and 1,600 fibers/mm-width or less and have a drape level of 120 mm or more and 240 mm or less.
2. The reinforcing fiber mat according to claim 1 , wherein the reinforcing fiber bundles are coated with an epoxy resin.
3. The reinforcing fiber mat according to claim 1 , wherein the reinforcing fiber bundles are coated with a polyamide resin.
4. The reinforcing fiber mat according to claim 1 , wherein the reinforcing fiber bundles have a bundle hardness of 39 g or more and 200 g or less.
5. The reinforcing fiber mat according to claim 1 , wherein the reinforcing fiber bundles have an average thickness of 0.01 mm or more and 0.2 mm or less.
6. The reinforcing fiber mat according to claim 1 , wherein the reinforcing fiber bundles have an average width of 0.03 mm or more and 3 mm or less.
7. The reinforcing fiber mat according to claim 1 , wherein the reinforcing fiber bundles have a width change rate W2/W1 of 0.5 or more and 1.1 or less.
8. The reinforcing fiber mat according to claim 1 , wherein the reinforcing fiber bundles have a sizing agent adhesion amount of 0.1 wt % or more and 5 wt % or less.
9. The reinforcing fiber mat according to claim 1 , wherein the reinforcing fiber bundles have an average fiber number of 86 or more and 4,000 or less.
10. The reinforcing fiber mat according to claim 1 , wherein the reinforcing fiber bundles have a cutting angle θ of 3° or more and 30° or less.
11. A fiber-reinforced resin forming material comprising a thermoplastic resin and the reinforcing fiber mat according to claim 1 .
12. A fiber-reinforced resin forming material comprising a thermoplastic resin and reinforcing fiber bundles and having a void ratio of 5 vol % or more and 30 vol % or less,
wherein the reinforcing fiber bundles contain single yarns by 500 fibers/mm-width or more and 1,600 fibers/mm-width or less and have a drape level of 120 mm or more and 240 mm or less.
13. A method of producing a fiber-reinforced thermoplastic resin forming material, comprising:
preparing a mat base material of reinforcing fiber bundles that contain single yarns by 500 fibers/mm-width or more and 1,600 fibers/mm-width or less and have a drape level of 120 mm or more and 240 mm or less;
dispersing or layering thermoplastic resin on the mat base material;
melting the thermoplastic resin; and
cooling and solidifying the melted thermoplastic resin between plates through a gap thicker by 5% or more than a thickness of a fully resin-impregnated base material.
14. A reinforcing fiber mat comprising reinforcing fiber bundles having an average fiber length of 5 mm to 100 mm,
wherein reinforcing fiber bundles consisting of 86 or more fibers per bundle are contained at a weight content of more than 99 wt % to 100 wt %, and
the reinforcing fiber bundles have a cutting angle θ of 3° or more and 30° or less.