Method for manufacturing a mold segment for curing and vulcanizing a tire
View Patent ↗A method for manufacturing an aluminium mould ( 1 ) segment ( 10 ) for curing and vulcanizing a tyre comprises: a) fixing at least one thin blade ( 2 ) for the formation of the grooves in the tire tread, in a mould form made of friable material, so that an exterior part of the thin blade is embedded in the material of the mould form and so that an interior part projects from this mould form, this thin blade being made from maraging steel and having been obtained by a selective laser melting method, b) closing the mould form and pouring or injecting aluminium into it, coating the interior part of the thin blade, c) breaking away the mould form to obtain the mould segment. The thin blade ( 2 ) is subjected to a peening treatment with a material with a Vickers hardness between 340 and 500 HV and with dimensions smaller than 0.3 mm.
1. A method for manufacturing an aluminum mold segment for curing and vulcanizing a tire, the method comprising:
(a) fixing at least one thin blade for formation of grooves in a tread of the tire in a mold form made of friable material, a shape of which is a negative of the mold segment that is to be obtained, such that an exterior part of the at least one thin blade is embedded in the material of the mold form and an interior part of the at least one thin blade projects from the mold form, the at least one thin blade being made from maraging steel and having been obtained by a selective laser melting method;
(b) closing the mold form and pouring or injecting aluminum into the mold form, coating the interior part of the at least one thin blade to fix it in place; and
(c) breaking the mold form to obtain the mold segment from a bottom of which the exterior part of the at least one thin blade projects,
wherein the at least one thin blade is subjected to a peening treatment including blasting it with shot particles made from a material with a Vickers hardness between 340 and 500 HV and with dimensions smaller than 0.3 mm.
2. The method according to claim 1 , wherein the shot particles are made of cast steel or of ceramic.
3. The method according to claim 1 , wherein the shot particles have a dimension of around 0.1 mm.
4. The method according to claim 1 , wherein a coverage of the peening treatment is between 200% and 600%.
5. The method according to claim 1 , wherein the peening treatment is performed at a pressure of between 1.5×10 5 Pa and 3.5×10 5 Pa.
6. The method according to claim 1 , wherein the peening treatment is performed before step (a).
7. The method according to claim 1 , wherein the peening treatment is performed after step (c).