One-piece woven vehicle occupant protection device and method for manufacturing the same
A method for manufacturing a one-piece woven (OPW) air bag includes providing yarns having a spin finish and warping the yarns on at least one beam of a loom. The yarns are simultaneously woven into a fabric air bag structure having two layer portions defining an inflatable volume and single layer portions forming seams delimiting the inflatable volume. The air bag structure is coated to cover the spin finish. The coated air bag structure is cut to define the one-piece woven air bag.
1. A method for manufacturing a one-piece woven (OPW) air bag, comprising:
providing yarns having a spin finish thereon;
warping the yarns on at least one beam of an air jet or rapier loom;
simultaneously weaving the yarns with the air jet or rapier loom into a fabric air bag structure having two layer portions defining an inflatable volume and single layer portions forming seams delimiting the inflatable volume;
coating the air bag structure with a coating formulated to adhere to the spin finish of the woven yarns; and
cutting the coated air bag structure to define the OPW air bag.
2. The method of claim 1 , wherein the coating comprises silicone.
3. The method of claim 2 , wherein the coating comprises a polyvinyl chloride (PVC) base coat that adheres to the spin finish.
4. The method of claim 2 , wherein the silicone coating includes a phosphate-based flame retardant material.
5. The method of claim 2 , wherein the silicone coating comprises an anti-blocking urethane.
6. The method of claim 2 , further comprising an anti-blocking urethane applied on the silicone coating.
7. The method of claim 1 , wherein the air bag structure is coated without scouring the yarns.
8. The method of claim 1 , wherein the air bag structure is coated without washing the yarns.
9. The method of claim 1 , wherein the air bag structure is coated without drying the yarns.
10. The method of claim 1 , wherein the coating has a T-peel adhesion with the air bag structure of about 0.78 to about 1.13.
11. The method of claim 1 , wherein the spin finish comprises about 1.0-3.0% by weight of the OPW air bag.
12. The method of claim 1 , wherein the air bag structure forms a side curtain.
13. An OPW air bag manufactured according to claim 1 .
14. The OPW air bag of claim 13 , wherein the OPW air bag forms a side curtain.
15. The method of claim 1 , wherein the step of coating the air bag structure comprises coating the airbag without scouring, washing, or drying the air bag structure.
16. The method recited in claim 1 , wherein the fabric airbag structure is coated in loom-state, free from scouring, heating, washing, or drying prior to the step of coating the loom-state OPW fabric structure.
17. A method for manufacturing a one-piece woven (OPW) air bag, comprising:
providing yarns having a spin finish thereon;
weaving the yarns with an air jet or rapier loom to form a loom-state OPW fabric structure having two layer portions defining an inflatable volume and single layer portions forming seams delimiting the inflatable volume;
coating the loom-state OPW fabric structure with a coating formulated to adhere to the spin finish of the woven yarns; and
cutting the coated air bag structure to define the OPW air bag.
18. The method recited in claim 17 , wherein the loom-state OPW fabric structure is free from scouring, heating, washing, or drying prior to the step of coating the loom-state OPW fabric structure.