3D printed microelectrode arrays
A high-density bioprobe array is provided comprising conductive or optical shanks. A method of making high-density bioprobe arrays also is provided. A bioprobe system using the array also is provided.
1. A method of preparing a high-density array of electrically-conductive, or optically-conductive shanks, comprising:
depositing by aerosol jet printing, a plurality of shanks onto a surface of a substrate in a density of greater than 100 shanks per square centimeter of the surface of the substrate, each shank having a diameter ranging from 10 μm to 1 mm, and a length ranging from 10 μm to 10 cm, wherein the shanks are formed by depositing over the surface of the substrate a plurality of layers of a shank material solution comprising a conductive material dispersed in a liquid or a waveguide-forming material in a solvent, where each layer of the plurality of layers is deposited as an open shape having ends and a gap defined by the ends.
2. The method of claim 1 , further comprising after deposition of every one to 50 layers, exposing the shanks to a heat or energy source to remove the liquid or solvent, and/or to at least partly crosslink the waveguide-forming material.
3. The method of claim 2 , wherein the shanks are exposed to continuous heat.
4. The method of claim 3 , wherein the continuous heat is from 90° C. to 110° C.
5. The method of claim 1 , wherein the shanks have an aspect ratio of diameter to length ranging from 1:1 to 1:1000.
6. The method of claim 1 , wherein gaps of one or more adjacent layers are offset with respect to each other.
7. The method of claim 1 , wherein layers are deposited to form a tapered shank.
8. The method of claim 1 , wherein one or more of the shanks is prepared by depositing a waveguide-forming material over a light-emitting diode (LED) on the substrate.
9. The method of claim 1 , wherein the substrate is a circuit board or an integrated circuit, wherein traces on the printed circuit board are deposited by aerosol jet printing.
10. The method of claim 1 , wherein an electrically-conductive material is deposited to form the conductive shanks.
11. The method of claim 10 , wherein the electrically-conductive material comprises metal nanoparticles, and further comprising sintering the metal nanoparticles.
12. The method of claim 11 , wherein the metal nanoparticles are sintered by raising the temperature to a temperature below the melting point of the metal nanoparticles at a rate of less than 5° C. per minute.
13. The method of claim 10 , further comprising depositing a conductive material over the conductive shank.
14. The method of claim 13 , wherein the conductive material comprises silver, gold, platinum, PEDOT (poly(3,4-ethylenedioxythiophene)), PEDOT-PSS (a poly(3,4-ethylenedioxythiophene) polystyrene sulfonate mixture), PEDOT-TMA (a poly(3,4-ethylenedioxythiophene)-tetramethacrylate copolymer), carbon black, or a conductive carbon allotrope.
15. The method of claim 14 , wherein the conductive carbon allotrope comprises graphene, graphite, a fullerene, a carbon nanotube, or vitreous carbon.
16. The method of claim 10 , further comprising depositing an insulator over a portion of at least one of the shanks, leaving a portion of the shank, exposed.
17. The method of claim 16 , wherein the tip of the shank is exposed.