V-ribbed belt and use thereof
A V-ribbed belt in which a friction transmission surface of a compression rubber layer is coated with a knit fabric is provided. The compression rubber layer is formed of the cured product of a rubber composition containing an ethylene-α-olefin elastomer and carbon black wherein the carbon black contains a soft carbon having a primary particle diameter of at least 40 nm and a hard carbon having a primary particle diameter of less than 40 nm. The ratio between the number of particles of the soft carbon and hard carbon is former/latter=3/97 to 25/75.
1. A V-ribbed belt comprising:
a compression rubber layer having a frictional power-transmission surface covered with a knitted cloth,
wherein
the compression rubber layer comprises a cured material of a rubber composition comprising an ethylene-α-olefin elastomer and a carbon black,
the carbon black comprises a soft carbon having a primary particle size of 40 nm or more and a hard carbon having a primary particle size of less than 40 nm,
a ratio of number of particles between the soft carbon and the hard carbon satisfies a relation of former/latter=3/97 to 15/85,
the rubber composition further comprises a staple fiber having a proportion of 10 parts by mass or lower with respect to 100 parts by mass of the ethylene-α-olefin elastomer, and
the carbon black has a proportion of 70 parts by mass or higher and 150 parts by mass or lower with respect to 100 parts by mass of the ethylene-α-olefin elastomer.
2. The V-ribbed belt according to claim 1 , wherein the soft carbon has an average primary particle size of 45 to 100 nm, and the hard carbon has an average primary particle size of 10 to 35 nm.
3. The V-ribbed belt according to claim 1 , wherein the carbon black has a proportion of 30 parts by mass or higher with respect to 100 parts by mass of the ethylene-α-olefin elastomer.
4. The V-ribbed belt according to claim 1 , wherein the rubber composition further comprises a vulcanizing agent and a crosslinking agent, and a total proportion of the vulcanizing agent and the crosslinking agent is 1 to 5 parts by mass with respect to 100 parts by mass of the ethylene-α-olefin elastomer.
5. The V-ribbed belt according to claim 1 , wherein the ethylene-α-olefin elastomer has a diene content of 1 to 3 mass %.
6. The V-ribbed belt according to claim 1 , wherein the ethylene-α-olefin elastomer has a Mooney viscosity (ML(1+4)125° C.) of 30 to 60.
7. Use of the V-ribbed belt according to claim 1 , under a belt tension of 30 to 120 N/rib.
8. The V-ribbed belt according to claim 1 , wherein the rubber composition further comprises a crosslinking agent, and a total proportion of the crosslinking agent is 1 to 5 parts by mass with respect to 100 parts by mass of the ethylene-α-olefin elastomer.
9. The V-ribbed belt according to claim 1 , wherein the rubber composition further comprises a vulcanizing agent, and a total proportion of the vulcanizing agent is 1 to 5 parts by mass with respect to 100 parts by mass of the ethylene-α-olefin elastomer.