US 12,272,471 · App. 16/974,145 · Granted Apr 8, 2025

Fine grain structures for tough rare earth permanent magnets

Inventors: Baozhi Cui (Ames, IA); Jun Cui (Ames, IA)
Assignee: Iowa State University Research Foundation, Inc.
H01F1/0557H01F1/058H01F1/059H01F7/02H01F41/0253
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,272,471
App. No.
16/974,145
Granted
Apr 8, 2025
Kind
B2
Abstract

The present invention provides fine grain structures for rare earth permanent magnets (REPMs) and their production in a manner to significantly enhance flexural strength and fracture toughness of the magnets with no or little sacrifice in the hard magnetic properties. The tough REPMs can have either homogeneous or heterogeneous refined grain microstructural architectures achieved by introducing a small amount of additive particle materials into the magnet matrix, such as fine-sized, insoluble, chemically stable, and non-reactive with the magnet matrix. These additive materials can act effectively as both heterogeneous nuclei sites and grain growth inhibitors during the heat treatment processes, which in turn resulting in refined grain structures of the REPMs. Alternatively, the fine grain structures were also achieved by using magnet alloy feedstock powders with finer particle sizes. The fine grains acting as the strengthening sites can inhibit the crack nucleation and can also slow down the propagation of micro-cracks, which in turn increasing magnet's fracture toughness.

Claims (14)

1. A sintered rare earth permanent magnet comprising at least one region comprised of a sintered feedstock blend of rare earth alloy feedstock particles and artificially-added grain-refining submicron feedstock particles having an average particle size of less than 1 micron wherein the sintered feedstock blend provides a refined grain microstructure that includes a rare earth alloy magnet matrix and the artificially-added grain-refining submicron feedstock particles dispersed in the microstructure which has an average refined grain size from about 15 to less than 40 microns, wherein the at least one region having the refined grain microstructure provides the sintered magnet with at least one of mechanical toughness and/or mechanical strength beneficial for inhibiting micro-cracking of the magnet.

2. The magnet of claim 1 that exhibits a flexural strength increase of 30% or greater at 20° C. compared to a flexural strength of only about 114 MPa of a sintered rare earth counterpart magnet having an average grain size of about 45 microns with no reduction of at least one of (BH) max , B r and H ci magnetic properties.

3. The magnet of claim 1 wherein the refined grain microstructure has an average grain size of about 22 to about 32 microns.

4. The magnet of claim 1 wherein the magnet has a heterogeneous grain structure that comprises regions having relatively fine grain size and coarse grain size wherein at least one of the regions has the sufficiently refined grain microstructure.

5. The magnet of claim 1 comprising represented by at least one of: R—cobalt including RCo 5 or R 2 Co 17 , R=rare earth, Lanthanum, or Yttrium; R-iron-boron including R 2 Fe 14 B or R-TM-B, TM is selected from a group of transition metals consisting essentially of Fe, Co and other transition metal elements; R-TM-carbon including R 2 Fe 14 C; a R-TM-nitrogen including R 2 Fe 17 X δ , R=rare earth, La, or Y; X=H, C, N, B, F, P, and/or S, and R-TM-M-nitrogen including R(Fe, M) 12 X δ , R=rare earth, La, or Y; M=Mo, V, Ti, Si, Al, Cr, Cu, Ga, Ge, Mn, Nb, Sn, Ta, W or Fe; X=H, C, N, B, F, P, and/or S.

6. The magnet of claim 1 comprising a rare-earth-transition metal based magnetic compound having the formula of R 2 TM 14 A, RTM 5 , RTM 17 , R 2 TM 17 A, RTM 7 , RTM 7 A, RTM 12 , RTM 12 A, R 3 TM 29 , or R 3 TM 29 A, wherein R is one or a combination of rare earths, La or Y, TM is one or a mixture of transition metals, A is one or a combination of the following elements: Be, B, C, N, S, Mg, Al, Si, P, Ga, Ge, As, Se, In, Sn, Sb, Te, I, Pb, or Bi.

7. The magnet of claim 1 which comprises consolidated powders.

8. A sintered rare earth permanent magnet comprising at least one region having a refined grain microstructure that includes a microstructure matrix and artificially-added grain-refining, submicron feedstock particles selected from at least one of carbide particles, fluoride particles, nitride particles, oxide particles, and/or sulfide particles dispersed in the mircostructure where they are non-reactive and insoluble without alteration of the matrix chemical composition and where the grain-refining submicron feedstock particles have an average particle size of less than 1 micron in the microstructure which has an average refined relatively fine grain size of about 22 to about 32 microns, wherein the at least one region having the refined grain microstructure provides the sintered magnet with at least one of mechanical toughness and/or mechanical strength beneficial for inhibiting micro-cracking of the magnet.

9. The sintered rare earth permanent magnet of claim 8 wherein the permanent magnet has a laminated microstructure that comprises said at least one region having the refined relatively fine grain size adjacent to another region having a relatively coarser grain size to form the laminated microstructure.

10. The magnet of claim 8 wherein the average particle size of the grain-refining submicron feedstock particles is about 0.35 micron or less.

11. The magnet of claim 8 which includes the artificially-added grain-refining, submicron feedstock particles in an amount of 0.5 to 10 weight %.

12. The magnet of claim 8 wherein said refined grain microstructure comprises the rare earth magnet alloy matrix comprised of sintered jet milled magnet alloy particles and the artificially-added grain-refining, submicron feedstock particles dispersed in the microstructure.

13. The magnet of claim 1 having a flexural strength of about 148 MPa or more.

14. The magnet of claim 1 wherein said refined grain microstructure comprises a matrix comprised of sintered jet milled feedstock particles and the artificially-added grain-refining, submicron feedstock particles dispersed in the microstructure.

Assignments (2)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Apr 29, 2021
From: CUI, BAOZHI; CUI, JUN
To: IOWA STATE UNIVERSITY RESEARCH FOUNDATION, INC.
Reel/Frame 056084/0853 →
CONFIRMATORY LICENSE Recorded Jan 15, 2021
From: IOWA STATE UNIVERSITY
To: UNITED STATES DEPARTMENT OF ENERGY
Reel/Frame 055009/0954 →
Continuity (2)
Provisional Application 62974009 · Nov 6, 2019
Related Publication 20210134497A1 · May 6, 2021
References Cited (18)
US 8377233B2 · Nakamura · 2013 [cited by examiner]
US 20050081960A1 · Liu · 2005 [cited by examiner]
US 20070071979A1 · Komuro · 2007 [cited by examiner]
US 20140210581A1 · Lewis · 2014 [cited by examiner]
US 20180151276A1 · Li · 2018 [cited by examiner]
US 20190115128A1 · Cui et al. · 2019 [cited by applicant]
CN 105931777A · 2016 [cited by examiner]
Wang, G. P. et al. “Effects of sintering temperature on the mechanical properties of sintered NdFeB permanent magnets prepared by spark plasma sintering,” Journal of Magnetism and Magnetic Materials, Aug. 27, 2013, vol.… [cited by examiner]
E. P. Wohlfarth et al, Handbook of Magnetic Materials, vol. 4, pp. 71-106 and 174-192, 1988. [cited by applicant]
F. Bittner et al, Normal and abnormal grain growth in fine-grained Nd—Fe—B sintered magnets prepared from He jet-milled powders, Journal of Magnetism and Magnetic Materials, 426, pp. 698-707, 2017. [cited by applicant]
J.F. Liu et al, Microstructure and magnetic properties of sintered NdFeB magnets with improved impact resistance, J. Appl. Phys., 97, 10H101 2005. [cited by applicant]
W. Li et al, Study on strengthening and toughening of sintered rare-earth permanent magnets, J.Appl. Phys. 105 07A703 2009. [cited by applicant]
Xiuyan Li et al, Playing with defects in metals, Nature Materials vol. 16, pp. 700, 2017. [cited by applicant]
Xiaolei Wu et al, Heterogeneous lamella structure unites ultrafine-grain strength wiith coarse-grain ductility, Proceedings of the National Academy of Sciences of the United States of America, 112, p. 14501, 2015. [cited by applicant]
Yinmin Wang et al, High tensile ductility in a nanostructured metal, Nature, vol. 419, p. 912, 2002. [cited by applicant]
P.F. Cesar et al, Relationship Between Fracture Toughness and Flexural Strength in Dental Porcelains, Journal of Biomedical Materials Research Part B Applied Biomaterials, 78, p. 265, 2006. [cited by applicant]
L.C. Stearns et al, Particle-Inhibited Grain Growth in Al2O3—SiC II, Equlibrium and Kinetic Analysis, J. Am. Chem. Soc., 79, pp. 3020, 1996. [cited by applicant]
AndreyV. Karasev et al, Effects of Oxide Particles and Solute Elements on Austenite Grain growth in Fe-0.05 mass % C and Fe-10 mass % Ni Alloys, ISJI International, vol. 48, No. 5, p. 658, 2008. [cited by applicant]