Method of making high quality silicon sulfide
A method is provided for making high quality silicon sulfide having 4N (99.99% by weight) or better purity.
1. A method of making silicon sulfide, comprising mixing silicon powder particles and sulfur powder particles in an inert atmosphere in a manner that coats the silicon powder particles with sulfur and prevents oxidation of the silicon powder particles wherein the sulfur powder particles provide an amount of sulfur that is present in an excess of stoichiometry of the silicon sulfide to be made, heating the sulfur-coated silicon particles disposed in a container to a final temperature for a time with motion of the container to react the silicon and the sulfur to form silicon sulfide reaction product, and removing excess sulfur from the silicon sulfide reaction product to produce the silicon sulfide with a purity of 4N (99.99% by weight on a trace metals basis) or better, wherein the mixing produces a powder mass consisting of the sulfur-coated silicon particles and excess sulfur.
2. The method of claim 1 wherein the mixing of the silicon powder particles and the sulfur powder particles is conducted by powder ball milling.
3. The method of claim 1 wherein the silicon powder particles have a diameter in a range of 1 to 20 microns.
4. The method of claim 1 wherein the motion of the container of the sulfur-coated silicon particles during heating produces the silicon sulfide reaction product as particulates.
5. The method of claim 1 wherein the container of the sulfur-coated silicon powder particles is disposed in a rotating furnace.
6. The method of claim 1 wherein the excess sulfur is removed by distillation of the excess sulfur from the silicon sulfide reaction product.
7. A method of making silicon sulfide, comprising ball milling silicon powder particles and sulfur powder particles in an inert atmosphere to produce ball milled powders in which the silicon powder particles are coated with sulfur and to prevent oxidation of the silicon powder particles wherein the sulfur powder particles provide an amount of the sulfur that is present in an excess of stoichiometry of the silicon sulfide to be made, heating the ball milled powders disposed in a container to a final temperature for a time with motion of the container to react the silicon and the sulfur to form silicon sulfide reaction product, and removing excess sulfur from the silicon sulfide reaction to produce the silicon sulfide with a purity of 4N (99.99% by weight on a trace metals basis) or better, wherein the mixing produces a powder mass consisting of the sulfur-coated silicon particles and excess sulfur.