Latent two-part polyurethane adhesives

1. A two-component polyurethane adhesive composition having a polyol component and an isocyanate component, wherein:

the polyol component comprises:

a) at least 35 weight percent, based on the weight of the polyol component, of a mixture of polyether polyols, the mixture of polyether polyols comprising

a-1) one or more polyether polyols each having a hydroxyl equivalent weight of 400 to 2000 and each being selected from homopolymers of propylene oxide and copolymers of 70 to 99% by weight propylene oxide and 1 to 30% by weight ethylene oxide, the one or more polyether polyols a-1) having an average nominal hydroxyl functionality of 2 to 4; and

a-2) one or more polyether polyols each having a hydroxyl equivalent weight of 100 to 399, the one or more polyether polyols a-2) having an average nominal functionality of at least 4, wherein the one or more polyether polyols a-2) are present in an amount of at least 2 weight percent, based on the weight of the polyol component;

b) one or more aliphatic diol chain extenders having a hydroxyl equivalent weight of up to 99;

c) 0 to 3 parts by weight per 100 parts by weight of a) of at least one compound having at least two primary and/or secondary aliphatic amine groups;

d) a catalytically effective amount of at least one urethane catalyst;

e) 5 to 60 weight percent, based on the weight of the polyol component, of at least one particulate filler, wherein the particulate filler includes precipitated calcium carbonate filler particles having a particle size of up to 200 nm;

and the polyisocyanate component comprises at least one organic polyisocyanate and 0 to 50% by weight, based on the total weight of the polyisocyanate component, of at least one particulate filler.

2. The two-component polyurethane adhesive of claim 1 wherein the precipitated calcium carbonate filler particles having a particle size of up to 200 nm constitute at least 2 wt-% of the polyol component.

3. The two-component polyurethane adhesive of claim 2 wherein the precipitated calcium carbonate filler particles having a particle size of up to 200 nm constitute at least 3.5 to 20 wt-% of the polyol component.

4. The two-component polyurethane adhesive of claim 1 wherein a-2) constitutes at least 2 weight-% of the polyol component.

5. The two-component polyurethane adhesive of claim 4 wherein a-2) constitutes 3 to 10 wt-% of the polyol component.

6. The two-component polyurethane adhesive of claim 1 wherein component e) includes at least one additional particulate filler, the additional particulate filler constituting 20 to 58 wt-% of the polyol component.

7. The two-component polyurethane adhesive of claim 1 , wherein d) includes at least one latent urethane catalyst.

8. The two-component polyurethane adhesive of claim 7 wherein the latent catalyst includes at least one catalyst selected from dibutyltin mercaptide, dioctyl tin mercaptide, dibutyltin thioglycolate and dioctyltin thioglycolate and at least one carboxylic acid- or phenol-blocked cyclic amidine catalyst.

9. The two-component polyurethane adhesive of claim 1 wherein the polyisocyanate component includes at least one polyisocyanate having an isocyanate equivalent weight of up to 350 and at least one one urethane group-containing, isocyanate-terminated prepolymer having at least 2 isocyanate groups per molecule and an isocyanate equivalent weight of 500 to 3500.

10. The two-component polyurethane adhesive of claim 1 wherein the polyisocyanate component includes 20 to 50 wt-%, based on the weight of the polyisocyanate component, of a particulate filler.

11. A cured adhesive formed by combining the polyol and polyisocyanate components of the two-component polyurethane adhesive of claim 1 to form an uncured adhesive, and then curing the uncured adhesive.

12. A method of bonding two substrates, comprising combining the polyol and polyisocyanate components of the two-component polyurethane adhesive of claim 1 to form an uncured adhesive, forming a layer of the uncured adhesive at a bondline between two substrates, and curing the uncured adhesive layer at the bondline to form a cured adhesive bonded to each of the substrates.

13. The method of claim 12 wherein the isocyanate index is 1.1 to 1.8.

14. The method of claim 12 wherein at least a portion of said curing is performed at a temperature of 0 to 35° C.

15. The method of claim 14 wherein a portion of said curing is performed at a temperature of 0 to 35° C. and a subsequent portion of said curing is performed at a temperature of 36 to 100° C.