Stannous oxide powder
The purpose of the present invention is to provide a stannous oxide, which has excellent solubility and resistance to oxidation, from a stannous oxide powder comprising a stannous oxide and inevitable impurities, the stannous oxide powder having a stannous oxide content of 99.99 mass % or more in dry mass, a specific surface area of less than 0.5 m 2 /g, a D50 particle size of 20 to 60 μm, and a half width of the particle size distribution of 5 to 30 μm.
1. A stannous oxide powder comprising stannous oxide and inevitable impurities, the stannous oxide powder having:
a stannous oxide content of 99.99% by mass or more in dry mass;
a specific surface area of less than 0.5 m 2 /g;
a D50 particle size of from 20 to 60 μm; and
a half width of a particle size distribution of from 5 to 30 μm.
2. The stannous oxide powder according to claim 1 , wherein a water content in stannous oxide is from 1 to 5 wt %.
3. The stannous oxide powder according to claim 1 , wherein the stannous oxide powder has a chlorine content of 1 ppm or less and a sulfur content of 10 ppm or less.
4. The stannous oxide powder according to claim 1 , wherein the stannous oxide powder has a sodium content of 5 ppm or less and a potassium content of 5 ppm or less.
5. The stannous oxide powder according to claim 1 , wherein the stannous oxide powder has an antimony content of 5 ppm or less.
6. The stannous oxide powder according to claim 1 , wherein the stannous oxide powder has a TAP density of from 1.0 to 4.0 g/cm 3 .
7. The stannous oxide power according to claim 1 , wherein when 100 g/L of stannous oxide powder is added to a solution having a methanesulfonic acid concentration of 100 g/L, the stannous oxide is dissolved in the solution for a time less than or equal to 30 seconds and has a turbidity after dissolution of 20 degrees.