Method for recovering unreacted alpha, beta-ethylenically unsaturated nitrile monomer contained in latex of carboxyl group-containing nitrile rubber
A method for recovering an unreacted α,β-ethylenically unsaturated nitrile monomer contained in a latex of a nitrile rubber obtained by emulsion polymerizing a monomer mixture comprising an α,β-ethylenically unsaturated nitrile monomer and a carboxyl group-containing monomer is provided. The method includes the steps of: adjusting a pH of the latex of the carboxyl group-containing nitrile rubber to 6.5 or more; decompressing the latex of the carboxyl group-containing nitrile rubber having the pH adjusted to 6.5 or more under a heating condition; and recovering a component evaporated by the decompression under the heating condition.
1. A method for recovering an unreacted α,β-ethylenically unsaturated nitrile monomer contained in a latex of a carboxyl group-containing nitrile rubber obtained by emulsion polymerizing a monomer mixture comprising an α,β-ethylenically unsaturated nitrile monomer, a carboxyl group-containing monomer, and a diene monomer, comprising the steps of:
adjusting a pH of the latex of the carboxyl group-containing nitrile rubber to 6.5 or more;
performing a treatment for removing the unreacted diene monomer before or after the step of adjusting the pH of the latex of the carboxyl group-containing nitrile rubber to 6.5 or more,
decompressing the latex of the carboxyl group-containing nitrile rubber having the pH adjusted to 6.5 or more that is obtained by removing the unreacted diene monomer under a heating condition; and
recovering a component evaporated by the decompression under the heating condition; wherein
a pressure reduction condition is −100 to −85 kPa in a gauge pressure when decompressing the latex of the carboxyl group-containing nitrile rubber under the heating condition, and
a pressure reduction condition in a treatment for removing the unreacted diene monomer is −70 to −50 kPa in a gauge pressure.
2. The method for recovering the unreacted α,β-ethylenically unsaturated nitrile monomer according to claim 1 , wherein the heating temperature is set to 40 to 80° C. when decompressing the latex of the carboxyl group-containing nitrile rubber under the heating condition.
3. The method for recovering the unreacted α,β-ethylenically unsaturated nitrile monomer according to claim 1 , wherein the latex of the carboxyl group-containing nitrile rubber is obtained by emulsion polymerizing the monomer mixture comprising the diene monomer, acrylonitrile and methacrylic acid.
4. The method for recovering the unreacted α,β-ethylenically unsaturated nitrile monomer according to claim 1 , wherein a polymerization conversion ratio in the emulsion polymerization is 60 to 95%.
5. The method for recovering the unreacted α,β-ethylenic ally unsaturated nitrile monomer according to claim 1 , wherein a temperature and a pressure in the treatment for removing the unreacted diene monomer are respectively lower than a heating temperature and a degree of pressure reduction when decompressing the latex of the carboxyl group-containing nitrile rubber under the heating condition.