CRACK-FREE GLASS SUBSTRATE CUTTING AND THINNING METHOD
A crack-free glass substrate cutting and thinning method, includes: an internal deformation line formation step in which an internal deformation line is formed inside a glass substrate at a predetermined distance from a surface of the glass substrate; a surface etching step in which the glass substrate is thinned by immersing the glass substrate in an etching solution such that a portion of the surface of the glass substrate, at which the internal deformation line is not formed, is etched and removed at a first etching rate; and an etch-cutting step in which, with the glass substrate immersed in the etching solution, the internal deformation line is etched and removed at a second etching rate higher than the first etching rate such that the glass substrate is cut along the internal deformation line.
1 . A crack-free glass substrate cutting and thinning method comprising:
an internal deformation line formation step in which an internal deformation line is formed inside a glass substrate at a predetermined distance from a surface of the glass substrate by irradiating the glass substrate with a laser beam at an intensity not exceeding an ablation threshold of the glass substrate;
a surface etching step in which the glass substrate is thinned by immersing the glass substrate in an etching solution such that a portion of the surface of the glass substrate, at which the internal deformation line is not formed, is etched and removed at a first etching rate; and
an etch-cutting step in which, with the glass substrate immersed in the etching solution, the internal deformation line is etched and removed at a second etching rate higher than the first etching rate such that the glass substrate is cut along the internal deformation line.
2 . The crack-free glass substrate cutting and thinning method according to claim 1 , wherein a thickness of the portion of the surface of the glass substrate removed in the surface etching step is smaller than a thickness of a portion with the internal deformation line formed thereon, which is removed in the etch-cutting step.
3 . The crack-free glass substrate cutting and thinning method according to claim 1 , wherein, in the internal deformation line formation step, phase transition from an α-phase to a β-phase occurs in a region inside the glass substrate corresponding to the internal deformation line.
4 . The crack-free glass substrate cutting and thinning method according to claim 3 , wherein, in the internal deformation line formation step, the internal deformation line is formed by inducing phase transition of a region inside the glass substrate ranging from an upper end of the internal deformation line to a lower end thereof without moving a focus of the laser beam.
5 . The crack-free glass substrate cutting and thinning method according to claim 3 , wherein, in the internal deformation line formation step, the internal deformation line is formed by inducing phase transition of a region inside the glass substrate corresponding to the internal deformation line while continuously moving a focus of the laser beam from an upper end of the region to a lower end thereof.
6 . The crack-free glass substrate cutting and thinning method according to claim 1 , wherein the glass substrate has a thickness of 100 μm or less.