Biaxially oriented polyester film
A biaxially oriented polyester film, which exhibits an excellent winding property in a manufacturing process, and realizes an excellent electromagnetic conversion property and less failure of signals of a magnetic recording tape to be produced thereof, is provided. This biaxially oriented polyester film satisfies the formula y≤−24.9X+3.8, where the protrusion height X is 0.075 μm, 0.100 μm, and 0.125 μm, and y denotes a base-10 logarithm value of the number of protrusions having protrusion heights of X or more in a visual field of a region of 282 μm×211 μm, and a protrusion height that corresponds to a 0.4% area of a bearing curve based on protrusion height distribution is 65-90 nm.
1. A biaxially oriented polyester film, wherein a logarithm value y of a protrusion frequency of protrusions having protrusion heights of X or more on at least one surface, which is measured by a contactless surface shape measurement device, satisfies a below relation formula (1), where the protrusion height X is 0.075 μm, 0.100 μm and 0.125 μm,
y≤− 24.9 X+ 3.8 (1)
(herein, X denotes a protrusion height (μm), y denotes a base-10 logarithm value of a protrusion number of protrusions having protrusion heights of X or more in a visual field of a region of 282 μm×211 μm), and
a protrusion height that corresponds to a 0.4% area of a bearing curve based on protrusion height distribution is 65 nm or more and less than 90 nm.
2. The biaxially oriented polyester film according to claim 1 , wherein polyester contained in the biaxially oriented polyester film has ethylene terephthalate or ethylene-2,6-naphthalenedicarboxylate as a main repeating unit.
3. The biaxially oriented polyester film according to claim 1 , wherein, when measuring the one surface and an other surface of the biaxially oriented polyester film by a contactless surface shape measurement device, center line average surface roughness of the one of the surfaces is higher than center line average surface roughness of the other surface by 1 nm or more.
4. The biaxially oriented polyester film according to claim 3 , comprising inert particles.
5. The biaxially oriented polyester film according to claim 3 , comprising two or more layers of different polyester layers laminated.
6. The biaxially oriented polyester film according to claim 1 , comprising inert particles.
7. The biaxially oriented polyester film according to claim 6 , comprising two or more layers of different polyester layers laminated.
8. The biaxially oriented polyester film according to claim 1 , comprising two or more layers of different polyester layers laminated.