Method of preparing electrocatalysts for converting carbon dioxide to chemicals
Electrocatalysts composed of single atoms or metal clusters dispersed over porous carbon support were prepared by a lithium-melt method. The new catalysts demonstrated high selectivity, high Faradic efficiency and low overpotential toward to the electrocatalytic reduction of carbon dioxide to chemicals.
1. A method of synthesizing a catalyst comprising:
adding a catalytic metal selected from the group consisting of Bi, and In in its metallic form to molten lithium metal;
atomically dispersing the catalytic metal in the molten lithium;
forming a lithium catalytic metal-solid;
converting a portion of lithium in the lithium catalytic metal solid to lithium hydroxide forming a catalytic metal-lithium hydroxide solid;
mixing said catalytic metal-lithium hydroxide solid with a conductive support material to form a mixture, the conductive support material being carbonaceous with a porous network and having catalytic metal decorated throughout the porous network;
removing lithium hydroxide from the mixture leaving a mixture of catalytic metal and the conductive support material; and
drying the mixture of catalytic metal and the conductive support material to produce the catalyst containing the catalytic metal atomically dispersed over the conductive support material.
2. The method of claim 1 , wherein converting the portion of the lithium-catalytic metal solid to catalytic metal-lithium hydroxide solid comprises reacting lithium in the lithium catalytic metal solid with moist air.
3. The method of claim 2 , further comprising mixing the catalytic metal-lithium hydroxide solid with the conductive support material using a mechanical method.
4. The method of claim 1 , wherein the atomic dispersion occurs in the molten lithium metal at a temperature of 300° C. or less.
5. The method of claim 1 , wherein removing the lithium hydroxide comprises a drop-wise washing of the catalytic metal lithium metal hydroxide solid with water thereby removing lithium.
6. The method of claim 5 , wherein the washing comprises forming an alkaline water solution and modifying the carbonaceous support with oxygenated species serving as anchoring sites for the catalytic metal.
7. The method of claim 1 wherein the catalytic metal is In.
8. The method of claim 7 , wherein the catalyst has a 0.1−55 wt % of In.
9. The method of claim 8 , where the catalyst has a Faradaic efficiency of at least 90% in converting of carbon dioxide to formate at −0.6 V (RHE).
10. The method of claim 1 , wherein the catalytic metal is Bi.
11. The method of claim 10 , wherein the catalyst has a 0.2−50 wt % of Bi.
12. The method of claim 11 , where the catalyst has a Faradaic efficiency of at least 90% in converting of carbon dioxide to formate at −0.6 V (RHE).
13. The method of claim 1 , wherein the catalytic metal is a bimetallic compound.