Titanium implant surfaces free from alpha case and with enhanced osteoinduction

1. An orthopedic implant having a titanium or titanium alloy body with a plurality of surfaces, the orthopedic implant produced according to a process comprising the operations of:

(a) additively building the orthopedic implant; and then

(b) mechanically, chemically, or mechanically and chemically eroding one or more surfaces of the orthopedic implant to (i) remove alpha case from, and (ii) impart an osteoinducting roughness including micro-scale structures or nano-scale structures into, the one or more surfaces.

2. The orthopedic implant according to claim 1 , wherein the one or more surfaces include surfaces within the interior of the body of the orthopedic implant.

3. The orthopedic implant according to claim 1 , wherein the one or more surfaces are configured to contact a bone or a bone graft material.

4. The orthopedic implant according to claim 1 , wherein the one or more surfaces are free surfaces.

5. The orthopedic implant according to claim 1 , wherein the operation (b) further comprises mechanically eroding the one or more surfaces of the orthopedic implant and, thereafter, chemically eroding the one or more surfaces.

6. The orthopedic implant according to claim 5 , wherein mechanically eroding the one or more surfaces of the orthopedic implant imparts the micro-scale structures into the one or more surfaces and chemically eroding the one or more surfaces of the orthopedic implant imparts the nano-scale structures into the one or more surfaces.

7. The orthopedic implant according to claim 6 , wherein the chemically eroded nano-scale structures overlap with the mechanically eroded micro-scale structures.

8. The orthopedic implant according to claim 7 , wherein the operation (a) of additively building the orthopedic implant yields macro-scale structures, which inhibit movement of the orthopedic implant, and the micro-scale structures, and the nano-scale structures overlap each other.

9. The orthopedic implant according to claim 1 , wherein treating comprises heating the implant to a temperature less than 80% of a melting temperature of the titanium or titanium alloy from which the implant is made, and at a pressure of at least 100 MPa.

10. The orthopedic implant according to claim 1 , further comprising: after operation (a), treating the orthopedic implant with hot isostatic pressure or hot uniaxial pressure, and wherein the treating operation is completed under vacuum or in an inert gas.

11. The orthopedic implant according to claim 1 , wherein the process further comprises the operation of applying a coating to the additively built orthopedic implant, before further processing, to block carbon, nitrogen, and oxygen from the one or more surfaces to be further processed.

12. The orthopedic implant according to claim 1 , wherein the operation (a) of additively building the orthopedic implant is completed by melting powder, particles, granules, wires, fragments, or combinations thereof of the titanium or titanium alloy into the shape of the orthopedic implant.

13. The orthopedic implant according to claim 1 , wherein the operation (a) of additively building the orthopedic implant is completed by sintering powder, particles, granules, wires, fragments, or combinations thereof of the titanium or titanium alloy into the shape of the orthopedic implant.

14. The orthopedic implant according to claim 1 , wherein the operation (a) of additively building the orthopedic implant comprises vertically additively building the orthopedic implant, and wherein vertically additively building comprises depositing a material layer to form a free surface of the one or more surfaces that does not contact bone, and successively depositing additional material layers to form a bone-contacting surface of the one or more surfaces that arises from edges of the material layers.

15. An orthopedic implant having a titanium or titanium alloy body with a plurality of surfaces, the orthopedic implant produced according to a process comprising the operations of:

a. additively building the orthopedic implant having one or more free surfaces and having one or more bone-contacting surfaces adapted to be placed in contact with bone, at least the one or more bone-contacting surfaces having a macro-scale roughness that inhibits movement of the orthopedic implant when the bone-contacting surfaces are placed in contact with bone; and then

b. sequentially mechanically and chemically eroding one or more of the one or more free surfaces and the one or more bone-contacting surfaces to (i) remove alpha case from, and (ii) impart an osteoinducting roughness including micro-scale structures and nano-scale structures into, one or more of the one or more free surfaces and the one or more bone-contacting surfaces.

16. The orthopedic implant according to claim 15 , wherein the macro-scale structures, the micro-scale structures, and the nano-scale structures overlap each other.

17. The orthopedic implant according to claim 15 , further comprising: after operation (a) treating the orthopedic implant with hot isostatic pressure or hot uniaxial pressure, and wherein treating comprises heating the implant to a temperature ranging from 1,643° F. to 1,751° F.±59° F. at a pressure of at least 100 MPa for a period of 180±60 minutes and then cooling to below 797° F.

18. The orthopedic implant according to claim 17 , wherein the treating step is completed under vacuum or in an inert gas.

19. The orthopedic implant according to claim 15 , wherein the process further comprises the operation of applying a coating to the additively built orthopedic implant, after the operation (a) and before further processing, to block carbon, nitrogen, and oxygen from the one or more surfaces to be further processed.

20. The orthopedic implant according to claim 15 , wherein the operation (a) of additively building the orthopedic implant is completed by melting or sintering powder, particles, granules, wires, fragments, or combinations thereof of the titanium or titanium alloy into the shape of the orthopedic implant.