Resin composition for camera module having excellent laser transmittance and camera lens module member produced using the same

1. A resin composition for a camera module comprising:

25 to 50 wt % of a polycarbonate resin;

5 to 30 wt % of a polycyclohexylenedimethylene terephthalate (PCT) resin;

30 to 50 wt % of a fibrous filler having a circular or elliptical cross-section; and

0.01 to 5 wt % of a dye,

wherein the PCT resin and the fibrous filler are included at a weight ratio of 1:3 to 1:5.

2. The resin composition of claim 1 , wherein the polycarbonate resin has a viscosity-average molecular weight (Mv) of 15,000 to 35,000.

3. The resin composition of claim 1 , wherein the PCT resin has an intrinsic viscosity of 0.6 to 0.8 dl/g.

4. The resin composition of claim 1 , wherein the fibrous filler comprises one or more of glass fiber, carbon fiber, silica fiber, potassium titanate fiber, titanium fiber, aramid fiber, and asbestos fiber.

5. The resin composition of claim 1 , wherein the fibrous filler has an average diameter of 3 to 15 μm and an average length of 0.05 to 5 mm.

6. The resin composition of claim 1 , further comprising one or more of a nucleating agent, a release agent, a compatibilizer, an antioxidant, an impact modifier, and an ultraviolet absorber.

7. The resin composition of claim 1 , which has a Charpy notched impact strength of 12 kJ/m 2 or more as measured for a 4-mm-thick specimen in accordance with ISO 180 standard (23° C.), and a laser transmittance of 80% or more as measured for a 2-mm-thick specimen at a wavelength of 980 nm.

8. The resin composition of claim 1 , wherein a specimen comprising a bonding portion having a size of 1.5 mm×60 mm×2.0 mm, formed by laser-welding the resin composition for a camera module with a laser-absorbing member at a wavelength of 980 nm, has a bonding strength (or maximum load value) of 2,500 N or more as measured at a speed of 50 mm/min using a UTM device.

9. The resin composition of claim 1 , which has a molding shrinkage rate of 0.5% or less as measured in accordance with ISO 294-4 standard, a linear thermal expansion coefficient of 40 to 50 (μm/m ° C.) as measured at a temperature ranging from −40 to 100° C. in accordance with ISO 11359 standard, and an average linear thermal expansion coefficient (an average of MD and TD values) of 25 to 60 as measured at a temperature ranging from −40 to 100° C. in accordance with ISO 11359 standard.

10. The resin composition of claim 1 , which has a flexural strength of 190 MPa or more and a flexural modulus of 9,000 MPa or more, as measured in accordance with the ISO 178 standard.

11. A camera module member produced using the resin composition for a camera module according to claim 1 .

12. The camera module member of claim 11 , which is a barrel or a rear body.