Three-dimensional printing of ceramic materials
An ink, and products formed from the ink, formulated at least in part from ceramic particles. The ink is formulated so that it can be used in additive manufacturing processes to form three-dimensional printed bodies. The three-dimensional printed bodies can have graded density and can be infiltrated by an infiltration material.
1. An ink for additive manufacturing, comprising:
an aqueous suspension of ceramic particles, wherein the aqueous suspension has a solid loading of the ceramic particles of at least 40 vol. %;
at least one viscosifier configured to increase the viscosity of the aqueous suspension; and
a pH modifier.
2. The ink of claim 1 , wherein the solid loading of the ceramic particles is in a range between 50 vol. % and 59 vol. %.
3. The ink of claim 1 , wherein the ceramic particles are formed from at least one ultra-high temperature ceramic material.
4. The ink of claim 1 , wherein the ceramic particles are formed from at least one of B 4 C, ZrB 2 , ZrC, HfC, and HfB 2 .
5. The ink of claim 1 , wherein the viscosifier is a nonionic, surfactant polyol.
6. The ink of claim 1 , wherein the viscosifier is provided in a range between 1 wt. % and 8 wt. %.
7. The ink of claim 1 , wherein the viscosifier is provided in a range between 4 wt. % and 8 wt. %.
8. The ink of claim 1 , wherein the ceramic particles have an average particle size in a range between 0.8 μm and 5 μm.
9. The ink of claim 1 , further comprising a dispersing agent.
10. The ink of claim 9 , wherein the dispersing agent is polyethyleneimine.
11. The ink of claim 1 , wherein the pH modifier is glacial acetic acid.
12. A method of preparing ink, comprising:
adding ceramic particles to deionized water to form a combination of ceramic particles and deionized water, wherein a quantity of the ceramic particles is added so that the combination has a solid loading of ceramic particles of at least 40 vol. %;
mixing the combination of ceramic particles and deionized water to disperse the ceramic particles in the deionized water to form an aqueous suspension;
adding a viscosifier to the aqueous suspension to increase the viscosity of the aqueous suspension; and
adding a pH modifier to the aqueous suspension.
13. The method of claim 12 , wherein the solid loading of the ceramic particles is in a range between 50 vol. % and 59 vol. %.
14. The method of claim 12 , wherein ceramic particles are added incrementally to the deionized water and mixed to form the aqueous suspension.
15. The method of claim 12 , wherein the viscosifier is a nonionic, surfactant polyol.
16. The method of claim 12 , further comprising adding a dispersing agent to the deionized water.
17. The method of claim 12 , wherein the pH modifier is glacial acetic acid.