Delayed cure additive manufacturing

1. A method for manufacturing a part having a completed shape, comprising

fabricating, in an additive fabrication stage, an object including build material for the part in an uncured or incompletely cured form and a solid mold forming a cavity comprising the completed shape and containing the build material; and

curing the part, in a curing stage that occurs after the additive fabrication stage;

wherein, in the additive fabrication stage, material that forms the object is deposited incrementally including depositing build material for the part in a liquid phase and depositing material for the solid mold, and during the additive fabrication stage the material for the solid mold solidifies to form the solid mold, the solid mold being removable by exposing said mold to a second temperature;

wherein the build material comprises a wax, a monomer, and a polymerization initiator and undergoes a phase change mechanism and a distinct polymerization mechanism, the phase change mechanism occurring during the additive fabrication stage and causing a phase change of the build material from a liquid to a non-liquid, the build material being curable by exposure to a first temperature lower than the second temperature;

wherein the distinct polymerization mechanism is initiated after the additive fabrication stage by heating the object including increasing a temperature of the object to the first temperature, the heating of the build material causing initiation of the distinct polymerization mechanism without causing removal of the solid mold, occurs during the curing stage, and occurs after the additive fabrication stage of the object, and cures the build material by the distinct polymerization mechanism,

wherein the process further comprises heating the object to the second temperature after the curing stage to remove the solid mold from the part.

2. The method of claim 1 , removal of the solid mold yields the part.

3. The method of claim 1 wherein the material for the solid mold solidifies by undergoing a physical phase change.

4. The method of claim 3 wherein undergoing the physical phase change includes allowing the material for the solid mold to cool.

5. The method of claim 1 wherein incrementally depositing material for the object includes depositing a plurality of layers of material.

6. The method of claim 5 wherein at least some layers of material of the plurality of layers of material are deposited using a jetting process.

7. The method of claim 5 wherein the material for the solid mold deposited in a second layer of the plurality of layers is deposited on the build material deposited in a first layer of the plurality of layers deposited prior to the second layer.

8. The method of claim 5 wherein at least some of the layers are added using two or more print heads.

9. The method of claim 5 wherein depositing the layers includes depositing a plurality of material components from a corresponding plurality of print heads, a first print head of the plurality of print heads depositing the polymerization initiator.

10. The method of claim 5 wherein incrementally depositing the layers further includes depositing at least some layers including only the material for the solid mold.

11. The method of claim 1 further comprising removing the solid mold.

12. The method of claim 1 wherein the build material comprises a liquid prior to the phase change mechanism.

13. The method of claim 1 wherein the build material undergoes a phase change of the build material to a liquid phase during the curing stage.

14. The method of claim 1 wherein the build material comprises a polymerization precursor.

15. The method of claim 1 , wherein the solid mold is substantially stable under a build curing condition.

16. The method of claim 1 , wherein the cured build material is substantially stable under a mold removal condition.

17. The method of claim 1 , wherein the non-liquid is sufficiently solidified for subsequent incremental deposit of material onto it during the additive fabrication stage.

18. The method of claim 1 , wherein during the curing stage and after the additive fabrication stage, the solid mold forms a solid cavity comprising the completed shape and holding the build material for the part in a liquid phase.

19. The method of claim 1 , wherein depositing the build material includes depositing the monomer as a first component from a first printhead and depositing the polymerization initiator as a second component from a second printhead.

20. The method of claim 19 , wherein:

the first component is deposited as a liquid and undergoes a phase change mechanism to become semi-solid,

the second component is deposited as a liquid and undergoes a phase change mechanism to become semi-solid, and

the first component and the second component are substantially unmixed when in the semi-solid form.

21. The method of claim 20 , wherein heating the object to the first temperature causes a second phase change mechanism occurring after the first phase change mechanism.

22. The method of claim 21 , wherein heating the object to the first temperature causes the first component of the build material and the second component of the build material to transition from semi-solid state to a liquid state, allowing the polymerization initiator and the monomer to mix.

23. The method of claim 1 , wherein the build material and the material for the solid mold are distinct materials.