INSULATED WIRE, COIL, AND ELECTRICAL OR ELECTRONIC EQUIPMENT
An insulated wire, containing a conductor and an insulating film (A) provided in contact with the conductor, in which the insulating film (A) contains polyaryletherketone, the polyaryletherketone has an exothermic peak at the range of 290 to 330° C. in a differential scanning calorimetry when the polyaryletherketone is cooled at a temperature falling rate of 10° C./min from a temperature equal to or higher than the melting temperature of the polyaryletherketone, and the half width of the exothermic peak is 6° C. or more.
1 . An insulated wire, comprising:
a conductor; and
an insulating film (A) provided in contact with the conductor;
wherein the insulating film (A) contains polyaryletherketone;
wherein the polyaryletherketone has an exothermic peak at the range of 290 to 330° C. in a differential scanning calorimetry when the polyaryletherketone is cooled at a temperature falling rate of 10° C./min from a temperature equal to or higher than the melting temperature of the polyaryletherketone; and wherein the half width of the exothermic peak is 6° C. or more.
2 . The insulated wire according to claim 1 , wherein the insulating film (A) is an extruded covering layer.
3 . The insulated wire according to claim 1 , wherein an insulating film (B) having different constituent material from that of the insulating film (A) is provided on the outer periphery of the insulating film (A).
4 . The insulated wire according to claim 3 , wherein the insulating film (B) comprises at least one kind of polyaryletherketone, polyetherimide, polyether sulphone, polyphenylene ether, polyphenylsulfone, polyimide, polyamide imide, a thermoplastic polyimide, and polyketone.
5 . The insulated wire according to claim 1 , wherein the polyaryletherketone contained in the insulating film (A) is polyetheretherketone.
6 . The insulated wire according to claim 1 , containing the polyaryletherketone in the insulating film (A) in an amount of 70 mass % or more.
7 . A coil, comprising the insulated wire according to claim 1 .
8 . An electrical or electronic equipment, comprising the coil according to claim 7 .
9 . A method of producing an insulated wire, comprising a step of forming an insulating film by extrusion-covering a resin containing a polyaryletherketone on the outer periphery of a conductor,
wherein the polyaryletherketone has an exothermic peak at the range of 290 to 330° C. in a differential scanning calorimetry when the polyaryletherketone is cooled at a temperature falling rate of 10° C./min from a temperature equal to or higher than the melting temperature of the polyaryletherketone; and
wherein the half width of the exothermic peak is 6° C. or more.
10 . The method according to claim 9 , wherein the polyaryletherketone is polyetheretherketone.
11 . A resin for an insulating film, comprising polyaryletherketone, wherein the polyaryletherketone has an exothermic peak at the range of 290 to 330° C. in a differential scanning calorimetry when the polyaryletherketone is cooled at a temperature falling rate of 10° C./min from a temperature equal to or higher than the melting temperature of the polyaryletherketone; and wherein the half width of the exothermic peak is 6° C. or more.
12 . The resin for an insulating film according to claim 11 , which is used for forming the insulating film by extrusion-covering the resin on the periphery of a conductor.
13 . The resin for an insulating film according to claim 11 , wherein the polyaryletherketone is polyetheretherketone.