Solid polymer electrolyte composition, and solid polymer electrolyte containing same

1. A solid polymer electrolyte composition comprising:

a polymer (A) comprising alkylene oxide and having one reactive double bond;

a multifunctional cross-linkable polymer (B); and

an ionic liquid, wherein the ionic liquid comprises N-methylacetamide and a lithium salt,

wherein N-methylacetamide and the lithium salt are present in a weight ratio of 40:60 to 60:40.

2. The solid polymer electrolyte composition according to claim 1 , wherein the polymer (A) comprises a polymerization unit derived from any one monomer selected from the group consisting of ethylene glycol methylether (meth)acrylate, ethylene glycol phenylether (meth)acrylate, diethylene glycol methylether (meth)acrylate, diethylene glycol 2-ethylhexylether (meth)acrylate, polyethylene glycol methylether (meth)acrylate, polyethylene glycol ethylether (meth)acrylate, polyethylene glycol 4-nonylphenylether (meth)acrylate, polyethylene glycol phenylether (meth)acrylate, ethylene glycol dicyclopenthenyl ether (meth)acrylate, polypropylene glycol methylether (meth)acrylate, polypropylene glycol 4-nonylphenylether (meth)acrylate or dipropylene glycol allylether (meth)acrylate, and combinations thereof.

3. The solid polymer electrolyte composition according to claim 1 , wherein the multifunctional crosslinkable polymer (B) comprises a polymerization unit derived from any one monomer selected from the group consisting of polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, trimethylolpropane ethoxylate triacrylate, trimethylolpropane propoxylate triacrylate, polypropylene glycol dimethacrylate, polypropylene glycol diacrylate, divinylbenzene, polyester dimethacrylate, divinylether, ethoxylated bisphenol A dimethacrylate, tetraethylene glycol diacrylate, 1,4-butanediol diacrylate, 1,6-hexandiol diacrylate, ditrimethylolpropane tetraacrylate, pentaerythritol tetraacrylate, pentaerythritol ethoxylate tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol hexaacrylate, trimethylolpropane trimethacrylate, and combinations thereof.

4. The solid polymer electrolyte composition according to claim 1 , wherein the polymer (A) is present in an amount of 5 parts by weight to 40 parts by weight relative to 100 parts by weight of the total composition.

5. The solid polymer electrolyte composition according to claim 1 , wherein the polymer (B) is present in an amount of 5 parts by weight to 30 parts by weight relative to 100 parts by weight of the total composition.

6. The solid polymer electrolyte composition according to claim 1 , wherein the ionic liquid is present in an amount of 50 parts by weight to 90 parts by weight relative to 100 parts by weight of the total composition.

7. The solid polymer electrolyte composition according to claim 1 , wherein the lithium salt is present in an amount of 10 parts by weight to 50 parts by weight relative to 100 parts by weight of the total composition.

8. The solid polymer electrolyte composition according to claim 1 , wherein the lithium salt comprises at least one selected from the group consisting of LiPF 6 , LiBF 4 , LiSbF 6 , LiAsF 6 , LiOH, LiOH·H 2 O, LiBOB, LiClO 4 , LiN(C 2 F 5 SO 2 ) 2 , LiN(CF 3 SO 2 ) 2 , CF 3 SO 3 Li, LiC(CF 3 SO 2 ) 3 , LiC 4 BO 8 , LiTFSI, and LiFSI.

9. A solid polymer electrolyte formed by photocuring the solid polymer electrolyte composition according to claim 1 .

10. The solid polymer electrolyte according to claim 9 , wherein a thickness of the electrolyte is 50 μm to 300 μm.

11. The solid polymer electrolyte according to claim 9 , wherein an ionic conductivity of the electrolyte is 1.0×10 −4 S/cm to 2.0×10 −3 S/cm based on 25° C.

12. An all solid-state battery comprising the solid polymer electrolyte according to claim 9 .