Polyimide resin composition
A polyimide resin composition obtained by blending a polyimide resin (A) and glass fiber (B), the polyimide resin (A) containing a repeating structural unit represented by the following formula (1) and a repeating structural unit represented by the following formula (2), a content ratio of the repeating structural unit of the formula (1) with respect to the total of the repeating structural unit of the formula (1) and the repeating structural unit of the formula (2) being 20 to 70 mol %, wherein R 1 represents a divalent group having from 6 to 22 carbon atoms containing at least one alicyclic hydrocarbon structure; R 2 represents a divalent chain aliphatic group having from 5 to 16 carbon atoms; and X 1 and X 2 each independently represent a tetravalent group having from 6 to 22 carbon atoms containing at least one aromatic ring.
1 . A polyimide resin composition, comprising:
a glass fiber; and
a polyimide resin mixed with the glass fiber and comprising a repeating structural unit of formula (1) and a repeating structural unit of formula (2),
wherein a content ratio of the repeating structural unit of the formula (1) with respect to the total of the repeating structural unit of the formula (1) and the repeating structural unit of the formula (2) is 25 mol % or more and less than 40 mol %, and the formula (1) and the formula (2) are
where R 1 is a divalent group of formula (R1-3), R 2 is a divalent chain aliphatic group having from 8 to 10 carbon atoms, X 1 and X 2 are a tetravalent group of formula (X-5),
wherein an amount of the glass fiber mixed in the polyimide resin composition is in a range of 30 to 65 mass % relative to a total mass of the polyimide resin composition,
wherein an average fiber length of the glass fiber is 3 to 6 mm, and
wherein the glass fiber is surface-treated with at least one selected from the group consisting of a urethane-based sizing agent and a urethane/epoxy-based sizing agent.
2 . The polyimide resin composition according to claim 1 , wherein the glass fiber is surface-treated with a urethane-based sizing agent.
3 . The polyimide resin composition according to claim 1 , wherein an inorganic filler other than the glass fiber is further mixed.
4 . The polyimide resin composition according to claim 3 , wherein an amount of the inorganic filler mixed is 0.05 to 15 mass % relative to a total mass of the polyimide resin composition.
5 . A molded article, comprising:
the polyimide resin composition of claim 1 .
6 . The polyimide resin composition according to claim 1 , wherein the amount of the glass fiber mixed in the polyimide resin composition is 50 to 65 mass % relative to a total mass of the polyimide resin composition.
7 . The polyimide resin composition according to claim 2 , wherein an inorganic filler other than the glass fiber is further mixed.
8 . The polyimide resin composition according to claim 7 , wherein an amount of the inorganic filler mixed is 0.05 to 15 mass % relative to a total mass of the polyimide resin composition.
9 . A molded article, comprising:
the polyimide resin composition of claim 2 .
10 . The polyimide resin composition according to claim 2 , wherein the amount of the glass fiber mixed in the polyimide resin composition is 50 to 65 mass % relative to a total mass of the polyimide resin composition.
11 . A molded article, comprising:
the polyimide resin composition of claim 3 .
12 . The polyimide resin composition according to claim 3 , wherein the amount of the glass fiber mixed in the polyimide resin composition is 50 to 65 mass % relative to a total mass of the polyimide resin composition.
13 . A molded article, comprising:
the polyimide resin composition of claim 6 .
14 . The polyimide resin composition according to claim 4 , wherein the amount of the glass fiber mixed in the polyimide resin composition is 50 to 65 mass % relative to a total mass of the polyimide resin composition.