Selective sinter-based fabrication of fully dense complexing shaped parts
The invention relates to a process for fabricating complex mechanical shapes from metal or ceramic, and in particular to fabricating complex mechanical shapes using a pressure-assisted sintering technique to address problems relating to variations in specimen thickness and tooling, or densification gradients, by 3-D printing of a sacrificial, self-destructing powder mold is created using e.g. alumina and swellable binders such as polysaccharides. The binder-free sintering powder that forms the manufactured item is injected into the mold, and high pressure is applied. The powder assembly can then be sintered by any pressure assisted technique to full densification and the self-destructing mold allows the release of the fully densified complex manufactured item.
1. A process for producing a sintered powder manufactured item, comprising the steps:
STEP 1—preparing a sacrificial powder mold of a manufactured item, the sacrificial powder mold made using 3D printing and the sacrificial powder of the sacrificial powder mold consisting of a high-temperature sintering powder and a swellable binder to create a self-destructible sacrificial powder mold when sintered;
STEP 2—loading a powder sintering material into the sacrificial powder mold to create a powder-mold assembly, wherein the powder sintering material is substantially free of binder;
STEP 3—applying isostatic pressure to the powder-mold assembly;
STEP 4—sintering of the powder-mold assembly; and
STEP 5—obtaining a sintered-powder cast manufactured item from the self-destructed sintered sacrificial powder mold.
2. The process of claim 1 , wherein the powder sintering material of STEP 2 is metal or ceramic.
3. The process of claim 1 , wherein the isostatic pressure of STEP 3 is at least 400 MPa.
4. The process of claim 1 , wherein the sintering of STEP 3 is at 1400 degrees Celsius for 4 hours under a heating rate of 3 degrees Celsius/minute.
5. The process of claim 1 , wherein the loading of STEP 2 includes a preliminary step of coating the sacrificial powder mold with a graphite spray.
6. The process of claim 1 , wherein the high-temperature sintering powder of STEP 1 is alumina, and the swellable binder of STEP 1 is selected from the group consisting of a polysaccharide, a mono-saccharide, a di-saccharide, a tri-saccharide, a starch, a carbohydrate, a saccharide derivative, and a mixtures and a combination thereof.
7. A method consisting of:
STEP 1—preparing a sacrificial powder mold of a dental crown, the sacrificial powder mold made using 3D printing and the sacrificial powder of the sacrificial powder mold consisting of a high-temperature alumina sintering powder and at least one swellable binder to create a self-destructible sacrificial powder mold when sintered;
STEP 2—loading a zirconia powder sintering material into the sacrificial powder mold to create a powder mold assembly, wherein the powder sintering material is substantially free of binder;
STEP 3—applying isostatic pressure to the powder-mold assembly;
STEP 4—sintering of the powder-mold assembly in a tube furnace; and
STEP 5—obtaining a sintered-powder cast zirconia dental crown from the self-destructed sintered sacrificial powder mold, wherein the relative density of the dental crown is about 99.42%.
8. The process of claim 7 , wherein the powder sintering material of STEP 2 is metal or ceramic.
9. The process of claim 7 , wherein the isostatic pressure of STEP 3 is at least 400 MPa.
10. The process of claim 7 , wherein the sintering of STEP 3 is at 1400 degrees Celsius for 4 hours under a heating rate of 3 degrees Celsius/minute.
11. The process of claim 7 , wherein the loading of STEP 2 includes a preliminary step of coating the sacrificial powder mold with a graphite spray.
12. The process of claim 7 , wherein the high-temperature sintering powder of STEP 1 is alumina, and the swellable binder of STEP 1 is selected from the group consisting of a polysaccharide, a mono-saccharide, a di-saccharide, a tri-saccharide, a starch, a carbohydrate, a saccharide derivative, and a mixtures and a combination thereof.
13. The method of claim 7 , wherein the zirconia powder sintering material is a 3 mol % yttria-stabilized zirconia powder.
14. The method of claim 7 , wherein the sacrificial powder mold of STEP 1 consists of 74% alumina, 13% powdered sugar and 13% maltodextrin.