Blue light cutting optical material having a bluish appearance

1. An optical material comprising:

at least one UV absorber that at least partially blocks light having a wavelength ranging from 400 to 450 nm;

at least one absorbing dye A having its maximum absorption wavelength in the range from 520 nm to 640 nm;

wherein the optical material:

is made of a material chosen from polythiourethane materials, polyurethane urea materials, materials resulting from the polymerization or copolymerization of polyepisulfide monomers or oligomers, and materials resulting from the polymerization or copolymerization of allylic monomers or oligomers;

has a colorimetric coefficient b* as defined in CIE (1976) L*a*b* international colorimetric system that is lower than or equal to 6, for an optical material thickness of 2 mm; and

has a hue angle h as defined in CIE (1976) L*a*b* international colorimetric system higher than or equal to 120º and lower than or equal to 180º, for an optical material thickness of 2 mm.

2. The optical material of claim 1 , further defined as having a hue angle h as defined in CIE (1976) L*a*b* international colorimetric system higher than or equal to 1200 and lower than or equal to 145º, for an optical material thickness of 2 mm.

3. The optical material of claim 1 , wherein said absorbing dye A has a maximum absorption wavelength in the range from 550 nm to 610 nm.

4. The optical material of claim 1 , wherein said absorbing dye A is an anthraquinone dye.

5. The optical material of claim 4 , wherein said absorbing dye A is Solvent Violet 33 or Solvent Violet 13.

6. The optical material of claim 1 , further defined as having a relative light transmission factor in the visible spectrum Tv, as defined in standard NF EN 1836, higher than or equal to 82%.

7. The optical material of claim 1 , further defined as having a colorimetric coefficient a* as defined in CIE (1976) L*a*b* international colorimetric system that is lower than or equal to 3, for an optical material thickness of 2 mm.

8. The optical material of claim 1 , further defined as having a colorimetric coefficient b* as defined in CIE (1976) L*a*b* international colorimetric system that is lower than or equal to 5.5, for an optical material thickness of 2 mm.

9. The optical material of claim 8 , further defined as having a colorimetric coefficient b* as defined in CIE (1976) L*a*b* international colorimetric system that is lower than or equal to 5, for an optical material thickness of 2 mm.

10. The optical material of claim 1 , further defined as being made of a material chosen from polythiourethane materials and materials resulting from the polymerization or copolymerization of polyepisulfide monomers or oligomers.

11. The optical material of claim 1 , wherein the absorbing dyes A are present in an amount ranging from 0.1 to 1000 ppm by weight, relative to the total weight of the optical material.

12. The optical material of claim 1 , wherein the UV absorbers are present in an amount ranging from 0.05 to 4% by weight, relative to the total weight of the optical material.

13. The optical material of claim 1 , further defined as not comprising any absorbing dye C having a maximum absorption wavelength of 500 nm or greater and less than 550 nm.

14. The optical material of claim 1 , further comprising at least one absorbing dye B having its maximum absorption wavelength in the range from 410 nm to 450 nm.

15. An optical article comprising a substrate with a front main face and a rear main face, wherein said substrate comprises the optical material of claim 1 .

16. The optical article of claim 15 , further defined as an ophthalmic lens.

17. An optical article comprising a substrate with a front main face and a rear main face, wherein said substrate comprises an optical material including at least one UV absorber that at least partially blocks light having a wavelength ranging from 400 to 450 nm, at least one absorbing dye A having its maximum absorption wavelength in the range from 520 nm to 640 nm, the optical material being made of a material chosen from polythiourethane materials, polyurethane urea materials, materials resulting from the polymerization or copolymerization of polyepisulfide monomers or oligomers, and materials resulting from the polymerization or copolymerization of allylic monomers or oligomers, the optical article:

having a colorimetric coefficient b* as defined in CIE (1976) L*a*b* international colorimetric system that is lower than or equal to 6, for an optical material thickness of 2 mm; and

having a hue angle h as defined in CIE (1976) L*a*b* international colorimetric system higher than or equal to 120º and lower than or equal to 180º, for an optical material thickness of 2 mm.

18. A method for manufacturing the optical material of claim 1 , comprising:

preparing an optical material composition by mixing at least one UV absorber that at least partially blocks light having a wavelength ranging from 400 to 450 nm, at least one absorbing dye A having its maximum absorption wavelength in the range from 520 nm to 640 nm, and a material or compounds chosen from a polythiourethane material or precursors thereof, a polyurethane urea material or precursors thereof, a material resulting from the polymerization or copolymerization of polyepisulfide monomers or oligomers or a precursor thereof, and a material resulting from the polymerization or copolymerization of allylic monomers or oligomers or a precursor thereof; and

curing said an optical material composition.