Method of preparing plant-based functional polyester filament
A plant-based functional polyester filament and a preparation method of the plant-based functional polyester filament are provided. The plant-based functional polyester filament includes polyester, and plant extract in a weight percentage range of approximately 0.1%-1.5%. The plant extract includes one or more of a peppermint extract, a valerian extract, a lavender extract, a wormwood extract, a chitin extract and a seaweed extract. The method includes preparing a plant-based functional polyester masterbatch, including: heating polyethylene terephthalate (PET) chips to a molten state, adding an antioxidant and a dispersant to the molten PET, stirring the molten PET, adding a protective agent and a plant extract to the molten PET, stirring the molten PET at a high speed, adding a modifier to the molten PET, obtaining a mixture by uniformly mixing the molten PET, and performing an extrusion granulation process on the mixture.
1. A preparation method of a plant-based functional polyester filament, comprising:
preparing a plant-based functional polyester masterbatch, including:
heating polyethylene terephthalate (PET) chips to a molten state at a temperature of approximately 250° C.-260° C.,
adding an antioxidant and a dispersant to the molten PET, and stirring the molten PET at a speed of approximately 500 rad/min-700 rad/min for approximately 10 minutes-15 minutes,
adding a protective agent and a plant extract to the molten PET, and stirring the molten PET at a high speed for approximately 20 minutes-40 minutes,
adding a modifier to the molten PET,
obtaining a mixture by uniformly mixing the molten PET and cooling to a temperature of approximately 220° C.-230° C., and
performing an extrusion granulation process on the mixture to obtain the plant-based functional polyester masterbatch.
2. The method according to claim 1 , wherein:
a mass ratio of the PET chips, the antioxidant, the dispersant, the protective agent, the plant extract and the modifier is approximately 100:(0.1-0.5):(0.1-0.3):(0.4-0.8):(0.5-5):(0.1-0.4).
3. A preparation method of a plant-based functional polyester filament, comprising:
preparing a plant-based functional polyester masterbatch, including:
heating polyethylene terephthalate (PET) chips to a molten state,
adding an antioxidant and a dispersant to the molten PET, and stirring the molten PET,
adding a protective agent and a plant extract to the molten PET, and stirring the molten PET at a high speed,
adding a modifier to the molten PET,
obtaining a mixture by uniformly mixing the molten PET, and
performing an extrusion granulation process on the mixture, wherein:
the antioxidant includes tert-butyl hydroquinone and zinc powder in a mass ratio of approximately 1:(2-5).
4. The method according to claim 1 , wherein:
the dispersant includes sodium tripolyphosphate, ethylenediaminetetraacetic acid and sodium pyrophosphate in a mass ratio of approximately 1:(1-4):(2-4).
5. A preparation method of a plant-based functional polyester filament, comprising:
preparing a plant-based functional polyester masterbatch, including:
heating polyethylene terephthalate (PET) chips to a molten state,
adding an antioxidant and a dispersant to the molten PET, and stirring the molten PET,
adding a protective agent and a plant extract to the molten PET, and stirring the molten PET at a high speed,
adding a modifier to the molten PET,
obtaining a mixture by uniformly mixing the molten PET, and
performing an extrusion granulation process on the mixture, wherein:
the protective agent includes nano-carbon powder and cross-linked chitosan porous microspheres in a mass ratio of approximately 1:(1-4).
6. The method according to claim 5 , wherein forming the cross-linked chitosan porous microspheres includes:
dissolving chitosan in an acetic acid solution with a mass concentration of approximately 2%-5%, and removing bubbles by standing still to obtain a uniform and transparent chitosan solution, wherein a mass ratio of the chitosan and the acetic acid solution is approximately 1:(95-100),
adding an emulsifier to liquid paraffin and nano-silica, and obtaining an emulsified dispersant by fully stirring, wherein a mass ratio of the liquid paraffin, the nano-silica and the emulsifier is approximately (50-60):(2-5): 1, and
under stirring condition, dropwise adding the chitosan solution to the emulsified dispersant, heating to a temperature of approximately 40° C.-50° C., after being uniformly mixed adding formaldehyde, adjusting a pH value of a reaction system to be approximately 4-5, and maintaining at a reaction temperature for approximately 2 hours-3 hours, after the reaction ends, water-washing the product, soaking the product with 20%-30% sodium hydroxide solution, and water-washing the product to obtain the cross-linked chitosan porous microspheres, wherein:
a mass ratio of the chitosan solution, the emulsified dispersant and the formaldehyde is approximately 100:(50-55):(4-8).
7. The method according to claim 1 , wherein:
the modifier includes ethylene bis-stearamide and silicone oil in a mass ratio of approximately 1:(3-5).
8. The method according to claim 1 , further including:
uniformly mixing the PET chips and the plant-based functional polyester masterbatch, melting the PET chips and plant-based functional polyester masterbatch by a screw extrusion, and extruding the melt from a spinning nozzle to obtain the plant-based functional polyester filament.
9. The method according to claim 8 , wherein:
a mass ratio of the PET chips and the plant-based functional polyester masterbatch is in a range of approximately (2-50): 1.
10. The method according to claim 8 , wherein:
a diameter of the spinning nozzle is approximately 5 μm-50 μm.
11. The method according to claim 1 , wherein:
breaking strength of the plant-based functional polyester filament is in a range of approximately 6.8 cN/dtex-7.8 cN/dtex,
elastic modulus of the plant-based functional polyester filament is in a range of approximately 90 cN/dtex-101 cN/dtex, and
elongation at break of the plant-based functional polyester filament is in a range of approximately 12%-18%.
12. The method according to claim 1 , wherein:
2000-times wear loss of the plant-based functional polyester filament is less than 0.001 g.
13. The method according to claim 1 , wherein:
a mite removal rate of the plant-based functional polyester filament is greater than 90%, and
antibacterial rates of Escherichia coli and Staphylococcus aureus of the plant-based functional polyester filament are greater than 98%.
14. The method according to claim 1 , wherein:
the plant extract includes one or more of a peppermint extract, a valerian extract, a lavender extract, a wormwood extract, a chitin extract and a seaweed extract.
15. The method according to claim 1 , wherein:
the antioxidant includes tert-butyl hydroquinone and zinc powder in a mass ratio of approximately 1:(2-5), and
the protective agent includes nano-carbon powder and cross-linked chitosan porous microspheres in a mass ratio of approximately 1:(1-4).
16. The method according to claim 3 , wherein:
the plant extract includes one or more of a peppermint extract, a valerian extract, a lavender extract, a wormwood extract, a chitin extract and a seaweed extract.
17. The method according to claim 3 , further including:
uniformly mixing the PET chips and the plant-based functional polyester masterbatch, melting the PET chips and plant-based functional polyester masterbatch by a screw extrusion, and extruding the melt from a spinning nozzle to obtain the plant-based functional polyester filament, wherein:
a mass ratio of the PET chips and the plant-based functional polyester masterbatch is in a range of approximately (2-50): 1.
18. The method according to claim 5 , wherein:
the plant extract includes one or more of a peppermint extract, a valerian extract, a lavender extract, a wormwood extract, a chitin extract and a seaweed extract.
19. The method according to claim 5 , further including:
uniformly mixing the PET chips and the plant-based functional polyester masterbatch, melting the PET chips and plant-based functional polyester masterbatch by a screw extrusion, and extruding the melt from a spinning nozzle to obtain the plant-based functional polyester filament, wherein:
a mass ratio of the PET chips and the plant-based functional polyester masterbatch is in a range of approximately (2-50): 1.