Suspension Medium for Improved Grit Delivery in Vapor Blast Operations
A suspension medium for improved grit delivery in vapor blast operations sets forth addition of a suspending-agent to a blast solution whereby solids are maintained in suspension absent agitation or mixing for at least 60 hours. The suspending agent increases the viscosity and/or density of the blast solution to increase the buoyancy force and/or acts as a dispersant and/or surfactant to maintain suspension of solids in solution over the extended time period. Different concentrations of suspending-agent may be employed with different grit and solid sized particles, depending on the application of vapor blasting at hand. The suspending-agent is preferably biodegradable.
1 . A suspension medium for improved grit delivery in vapor blast operations comprising:
2% suspending-agent by weight;
98% water by weight; and
grit added at a weight ratio of 1 part grit to a range of 1 to 5 parts blast solution.
2 . The suspension medium of claim 1 wherein the suspending-agent is a dispersant.
3 . The suspension medium of claim 1 wherein the suspending-agent is a surfactant.
4 . The suspension medium of claim 1 wherein suspending-agent increases the density of the water and thereby increases the buoyancy force of the suspended grit particles.
5 . The suspension medium of claim 1 wherein the suspending-agent is a biodegradable compound.
6 . The suspension medium of claim 5 wherein the suspending-agent is xanthan gum.
7 . The suspension medium for improved grit delivery in vapor blast operations of claim 1 wherein the grit is added at a weight ratio of 1 part grit to 3 parts blast solution.
8 . In an apparatus for wet blasting, a method for improved wet or vapor blast operations comprising addition of a suspending-agent to a blast solution interior to the blast pot wherein settling of grit particles within the blast solution is prevented without the need for agitation of the blast solution as would otherwise be required.
9 . The method of claim 8 wherein an amount of the suspending-agent additional to the blast solution comprises between 1 to 3% of the suspending-agent by weight.
10 . The method of claim 8 further comprising the step of adding grit to the blast solution at a range of ratios of 1:1 to 1:5 parts grit to water.
11 . The method of claim 10 wherein the grit to blast solution ratio is 1 part grit to 3 parts water.