Three dimensional multiphasic structures via vaporization induced phase separation (VIPS)
This disclosure demonstrates a new method to produce three dimensional multiphasic structures, including bijels, via vapor-induced phase separation (VIPS). In VIPS, the evaporation of the co-solvent from a ternary mixture of oil, water and ethanol, induces phase separation. Particles present in the mixture attach to the interface and arrest the phase separation between water and oil. VIPS enables, inter alia, the fabrication of films and coatings via spreading or spraying particle-laden suspension onto a surface without the need for an outer aqueous phase.
1. A method, comprising:
with a ternary mixture of a hydrophilic phase, an organic phase, and a co-solvent, the ternary mixture further having a plurality of particles disposed therein,
giving rise to evaporation of the co-solvent into the environment exterior to the ternary mixture,
the evaporation effecting (1) a phase separation that forms an interface between the hydrophilic phase and the organic phase, and (2) an assembly of at least some of the plurality of particles at the interface,
the assembly arresting the phase separation and the evaporation giving rise to a multiphasic three-dimensional structure,
the multiphasic three-dimensional structure defining a plurality of domains therein.
2. The method of claim 1 , wherein the multiphasic three-dimensional structure is characterized as being a bicontinuous structure, a cellular structure, or a double-emulsion structure.
3. The method of claim 2 , wherein the multiphasic three-dimensional structure is characterized as being a bicontinuous structure.
4. The method of claim 2 , wherein the multiphasic three-dimensional structure defines a thickness in the Z-direction.
5. The method of claim 4 , wherein discrete domains located at different positions along the Z-direction define different average cross-sectional dimensions.
6. The method of claim 4 , wherein the thickness is in the range of from about 1 micrometers to about 10,000 micrometers.
7. The method of any claim 1 , further comprising (a) applying the ternary mixture to a substrate or (b) expressing the ternary mixture into the environment.
8. The method of claim 1 , wherein the co-solvent comprises an alcohol, acetone, tetrahydrofuran, or any combination thereof.
9. The method of claim 1 , wherein the plurality of particles comprises polymeric particles, metal particles (including alloys), metal oxide particles, naturally-occurring particles, or any combination thereof.
10. The method of claim 9 , wherein the metal oxide particles comprise zinc oxide particles, titanium dioxide particles, or both.
11. The method of claim 1 , wherein the method is performed under ambient conditions.
12. The method of claim 1 , wherein the method is performed under reduced humidity conditions.
13. The method of claim 1 , wherein the method is performed under increased humidity conditions.
14. The method of claim 1 , further comprising effecting motion of an atmosphere over the ternary mixture so as to modulate the evaporation of the co-solvent.
15. The method of claim 1 , wherein at least one of the organic phase and the hydrophilic phase comprises a polymerizable monomer.
16. The method of claim 15 , further comprising polymerizing the monomer.
17. The method of claim 1 , wherein the method is performed so as to form the three-dimensional structure in a continuous manner.
18. The method of claim 1 , wherein the method is performed so as to form the three-dimensional structure in a batch manner.