Polyamide composition and molded article made of the same with improved mechanical strength and reduced weight
Disclosed herein are a polyamide composition and a molded article made of the same with improved mechanical strength and reduced weight. The molded article may include the polyamide composition that includes high flowable polyamide and polyphthalamide and a small-diameter fiber, thereby resulting in an improvement in mechanical strength while achieving excellent surface properties and high weight reduction.
1. A polyamide composition comprising:
a primary resin comprising polyamide;
a secondary resin comprising polyphthalamide;
a fiber; and
a heat-resistant agent,
wherein the polyamide comprises one or more selected from the group consisting of polyamide 6, polyamide 66, polyamide 12, polyamide 6/66, polyamide 6/12, and polyamide 6/6T,
wherein the polyphthalamide comprises polyphthalamide 6I,
wherein the fiber comprises one or more selected from the group consisting of a glass fiber, a metal fiber, a carbon fiber, and a natural fiber,
wherein the polyamide composition comprises the primary resin in an amount of about 50 to 58.5 parts by weight and the secondary resin in an amount of about 5.8 to 14.2 parts by weight, based on 100 parts by weight of the fiber.
2. The polyamide composition of claim 1 , wherein the polyphthalamide has a coefficient of thermal expansion (CTE) of about 55.0 μm/m° C. to 70.0 μm/m° C. at a temperature of about 23° C. to 55° C., a melting point of about 260° C. to 300° C., and a glass transition temperature of about 110° C. to 150° C.
3. The polyamide composition of claim 1 , wherein the fiber has a diameter of about 10 μm to 17 μm.
4. The polyamide composition of claim 1 , wherein the heat-resistant agent comprises one or more selected from the group consisting of a phosphorus compound, a sulfur compound, and a metal salt compound.
5. The polyamide composition of claim 1 , wherein the polyamide composition comprises the heat-resistant agent in an amount of about 1.6 to 3.4 parts by weight based on 100 parts by weight of the fiber.
6. A molded article produced by mixing a polyamide composition of claim 1 and injection molding thereof.
7. The molded article of claim 6 , wherein the molded article has a tensile strength of about 315 MPa or more measured according to ISO 527, a flexural strength of about 450 MPa or greater measured according to ISO 178, and a Charpy impact strength of about 35 KJ/m 2 or greater measured according to ISO 179/1eA.