Diisocyanate composition, preparation method thereof and optical material using same
The diisocyanate composition according to an embodiment of the present invention comprises, in the composition, a benzyl isocyanate having a methyl group in an amount of 5 ppm to 200 ppm, an aromatic compound having a halogen group in an amount of 5 ppm to 1,000 ppm, a benzyl isocyanate having an ethyl group in an amount of 1 ppm to 1,000 ppm, or a combination thereof. It is possible to improve the optical characteristics by preventing the occurrence of yellowing, striae, and cloudiness and to enhance the mechanical properties such as impact resistance at the same time. Thus, it can be advantageously used to prepare an optical material of high quality.
1. A composition comprising
m-xylene diisocyanate in an amount of 99.5% by weight to less than 100% by weight based on the total weight of the composition; and
a compound of Formula I in an amount of 5 ppm to 200 ppm by weight based on the total weight of the composition, a compound of Formula II in an amount of 5 ppm to 1,000 ppm by weight based on the total weight of the composition, a compound of Formula III in an amount of 1 ppm to 1,000 ppm by weight based on the total weight of the composition, or a combination thereof
2. The composition of claim 1 , further comprising p-xylylene diisocyanate in an amount of greater than 0% by weight to 0.5% by weight based on the total weight of the composition.
3. The composition of claim 1 , further comprising a thiol or an episulfide.
4. An optical material comprising a cured product of a composition, the composition comprises
m-xylene diisocyanate in an amount of 99.5% by weight to less than 100% by weight based on the total weight of the composition; and
a compound of Formula I in an amount of 5 ppm to 200 ppm by weight based on the total weight of the composition, a compound of Formula II in an amount of 5 ppm to 1,000 ppm by weight based on the total weight of the composition, a compound of Formula III in an amount of 1 ppm to 1,000 ppm by weight based on the total weight of the composition, or a combination thereof
5. The optical material of claim 4 , wherein the composition further comprises a thiol or an episulfide.
6. The optical material of claim 4 , which has an impact resistance energy (E) of 0.4 J to 4.0 J, a transmittance of 90% or more, and a yellow index of 22 or less.