Process for reinforcing continuous fiber additively manufactured laminates
A method for fabricating a composite part using a 3D printing machine. The method includes forming the part by depositing a plurality of part layers in a consecutive manner on top of each other where each layer is deposited by laying down rows of filaments made of a thermoplastic composite material. Reinforcing Z-pins are then inserted through the part layers to provide reinforcement of the part in the Z-direction. A plurality of additional part layers are deposited in a consecutive manner on top of each other on the part layers including the reinforcing Z-pins where each additional part layer is also deposited by laying down rows of filaments made of a thermoplastic composite material. Reinforcing Z-pins are also inserted through the additional part layers to provide reinforcement of the part in the Z-direction.
1. An automated method for fabricating a composite part, said method comprising:
depositing a plurality of part layers in a consecutive manner on top of each other in the X and Y directions where each layer is deposited by laying down rows of filaments made of a thermoplastic composite material;
inserting reinforcing Z-pins through the part layers to provide reinforcement of the part in the Z-direction; and
depositing a plurality of additional part layers in a consecutive manner on top of each other where each additional layer is deposited by laying down rows of the filaments made of the thermoplastic composite material on the part layers including the reinforcing Z-pins and inserting the reinforcing Z-pins through the additional part layers to provide reinforcement of the part in the Z-direction.
2. The method according to claim 1 wherein at least some of the reinforcing Z-pins in the part layers and the additional part layers are off-set from each other and are not aligned.
3. The method according to claim 1 wherein inserting the reinforcing Z-pins includes inserting the Z-pins all of the way through the part layers.
4. The method according to claim 1 wherein inserting the reinforcing Z-pins includes inserting the Z-pins part way through the part layers.
5. The method according to claim 1 wherein inserting the reinforcing Z-pins includes inserting the Z-pins so that a back end of the Z-pins stick up from the part layers.
6. The method according to claim 1 wherein inserting the reinforcing Z-pins includes providing a higher density of the Z-pins at one location than at other locations.
7. The method according to claim 6 wherein inserting the reinforcing Z-pins includes transitioning the areal density of the Z-pins from the higher density location to a lower density location.
8. The method according to claim 1 wherein inserting the reinforcing Z-pins through the part layers includes ultrasonically vibrating the Z-pins and forcing them into the part layers.
9. The method according to claim 1 wherein inserting the reinforcing Z-pins through the part layers includes forming a plurality of holes through the part layers and then inserting the reinforcing Z-pins in the holes.
10. The method according to claim 9 wherein forming the plurality of holes includes using at least one needle.
11. The method according to claim 10 wherein forming the plurality of holes includes ultrasonically vibrating the at least one needle.
12. The method according to claim 10 wherein forming the plurality of holes includes heating the at least one needle.
13. The method according to claim 10 wherein forming the plurality of holes includes inserting a plurality of needles at the same time into the part layers.
14. The method according to claim 9 wherein forming the plurality of holes includes using at a solvent.
15. The method according to claim 1 wherein the Z-pins are rods.
16. The method according to claim 15 wherein the rods are carbon fiber pultruded rods.
17. The method according to claim 1 wherein the thermoplastic composite material is carbon fiber in a thermoplastic matrix.
18. A method for fabricating a composite part, said method comprising:
depositing a plurality of part layers in a consecutive manner on top of each other in the X and Y directions where each layer is deposited by laying down rows of filaments made of a thermoplastic composite material;
inserting reinforcing rods through the part layers to provide reinforcement of the part in the Z-direction so that at least some of the reinforcing rods stick up from the part layers;
depositing a plurality of additional part layers in a consecutive manner on top of each other in the X and Y directions where each additional layer is deposited by laying down rows of the filaments made of the thermoplastic composite material on the part layers including the reinforcing rods; and
inserting the reinforcing rods through the additional part layers to provide reinforcement of the part in the Z-direction.
19. The method according to claim 18 wherein inserting the reinforcing rods includes providing a higher density of the rods at one location than at other locations.