System for and method of linking by friction welding a first piece of steel to a second piece of steel with use of Ni-based alloys adapter
A system is provided, comprising a two-sided adapter, made of a Ni-based alloy, that is connected at each of the two sides with a different type of metal, e.g. steel, and wherein the connection of the different types of metal, e.g. steel with the adapter is characterized in that it is achieved at least in part by use of friction welding. A method for linking different types of metal, e.g. steel by using a two-sided adapter as an intermediate, wherein at least one of the adapter-metal (e.g. steel) connections is made by means of friction welding, is also provided.
1. A method for preparing a three-piece spacer for connecting dissimilar metals, the three-piece spacer consisting of a first piece, a two-sided adapter connected to the first piece on a first side of the two-sided adapter, and a third piece connected to a second side of the two-sided adapter opposite the first side, the method comprising:
preparing a two-piece spacer consisting of the first piece and the two-sided adapter; and
welding the third piece to the second side of the two-sided adapter of the two-piece spacer to obtain the three-piece spacer,
wherein:
the first piece is a tubular piece of a first metal, the first metal having a first chromium content;
the two-sided adapter consists of a tubular piece of a nickel-based alloy, the nickel-based alloy having a second chromium content;
the third piece is a tubular piece of a second metal, the second metal having a third chromium content;
the second chromium content is equal to either the first chromium content or the third chromium content;
the first chromium content is different from the third chromium content; and
either (1) or (2) applies to the method, or both (1) and (2) apply to the method:
(1) the two-piece spacer is prepared by rotational friction welding of the first piece and the two-sided adapter;
(2) the third piece is welded to the two-piece spacer by rotational friction welding.
2. The method of claim 1 , wherein the two-piece spacer is prepared by rotational friction welding of the first piece and the two-sided adapter.
3. The method of claim 1 , wherein the third piece is welded to the two-piece spacer by rotational friction welding.
4. The method of claim 1 , wherein:
the two-piece spacer is prepared by additive manufacturing the nickel-based alloy onto an end of the first piece; and
the third piece is welded to the two-piece spacer by rotational friction welding.
5. The method of claim 1 , wherein:
the two-piece spacer is prepared by laser beam welding of the first piece and the two-sided adapter; and
the third piece is welded to the two-piece spacer by rotational friction welding.
6. The method of claim 1 , wherein:
the two-piece spacer is prepared by rotational friction welding of the first piece and the two-sided adapter; and
the third piece is welded to the two-piece spacer by laser beam welding.
7. The method of claim 1 , wherein:
the two-piece spacer is prepared by rotational friction welding of the first piece and the two-sided adapter; and
the third piece is welded to the two-piece spacer by rotational friction welding.
8. The method of claim 1 , wherein the first metal and the second metal are steels.
9. The method of claim 1 , wherein the first metal or the second metal is a martensitic steel.
10. The method of claim 9 , wherein the Ni-based alloy is EPRI P87 alloy, A617 alloy, or A82 alloy.
11. The method of claim 1 , wherein the first metal or the second metal is an austenitic steel.
12. The method of claim 11 , wherein the Ni-based alloy is EPRI P87 alloy, A617 alloy, or A82 alloy.
13. The method of claim 12 , wherein:
the first metal is a martensitic steel; and
the second metal is an austenitic steel.
14. The method of claim 1 , wherein:
the first metal is a martensitic steel; and
the second metal is an austenitic steel.
15. The method of claim 1 , wherein:
the first metal is an austenitic steel; and
the second metal is a martensitic steel.
16. The method of claim 1 , wherein:
the first metal is an austenitic steel; and
the second metal is a second nickel-based alloy differing from the nickel-based alloy of the two-sided adapter.
17. The method of claim 1 , wherein:
the first metal is a martensitic steel;
the first chromium content is from 8% to 13% by weight;
the second metal is an austenitic steel; and
the third chromium content is from 17% to 35% by weight.
18. The method of claim 1 , wherein:
the first metal is a martensitic steel;
the first chromium content is from 8% to 13% by weight;
the second metal is an austenitic steel;
the third chromium content is from 17% to 35% by weight; and
the Ni-based alloy is EPRI P87 alloy, A617 alloy, or A82 alloy.
19. The method of claim 1 , wherein the two-sided tubular adapter has a ring shape or a donut shape and the first piece and the second piece are hollow tubes.
20. The method of claim 1 , wherein the third piece is welded to the two-piece spacer by rotational friction welding, the method further comprising:
providing end surfaces on the second side of the two-sided tubular adapter prior to welding the third piece, wherein the end surfaces are not perpendicular with respect to a longitudinal axis of the two-sided adapter.