Method for manufacturing semiconductor structure with reduced nodule defects
A method for removing nodule defects is disclosed. The nodule defects may be formed on a non-selected portion of a semiconductor structure during formation of a semiconductor region on a selected portion of the semiconductor structure. A plasma having a higher selectivity to etch the nodule defects relative to the semiconductor region may be used to selectively remove the nodule defects on the non-selected portion.
1. A method for eliminating nodule defects which are formed on a non-selected portion of a semiconductor structure during formation of a semiconductor region on a selected portion of the semiconductor structure, the method comprising
applying to the semiconductor structure a plasma which has a higher selectivity to etch the nodule defects relative to the semiconductor region, to thereby eliminate the nodule defects,
wherein the nodule defects have an amorphous phase, and the semiconductor region has a crystalline phase.
2. The method of claim 1 , wherein the plasma is generated from a gas source including hydrogen.
3. The method of claim 2 , wherein a flow rate of the hydrogen is controlled in a range from 10 sccm to 2000 sccm.
4. The method of claim 2 , wherein the gas source further includes a carrier gas selected from helium, argon, and a combination thereof.
5. The method of claim 4 , wherein a flow rate of the carrier gas is controlled in a range from 50 sccm to 6000 sccm.
6. The method of claim 1 , wherein the plasma is operated under a temperature ranging from 90° C. to 600° C.
7. The method of claim 1 , wherein the plasma is operated under a pressure ranging from 0.05 torr to 6 torr.
8. The method of claim 1 , wherein the plasma is generated by a plasma generation source selected from a transformer-coupled plasma generator, an inductively coupled plasma system, a magnetically enhanced reactive ion etching system, an electron cyclotron resonance system, or a remote plasma generator.
9. A method for manufacturing a semiconductor structure, comprising:
forming two first recesses in two first regions of a first semiconductor portion;
forming first source-drain regions in the first recesses; and
applying a plasma to eliminate nodule defects formed on a dielectric portion, the plasma having a higher selectivity to etch the nodule defects relative to the first source-drain regions so as, to eliminate the nodule defects,
wherein the nodule defects have an amorphous phase, and the first source-drain regions have a crystalline phase.
10. The method of claim 9 , after forming the first source-drain regions, further comprising:
forming two second recesses in two second regions of a second semiconductor portion; and
forming second source-drain regions in the second recesses of the second semiconductor portion.
11. The method of claim 10 , wherein the nodule defects are formed in at least one of forming the first source-drain regions and forming the second source-drain regions, and the plasma has a higher selectivity to etch the nodule defects relative to the first source-drain regions and the second source-drain regions.
12. The method of claim 10 , wherein the second source-drain regions have a crystalline phase.
13. The method of claim 12 , wherein the plasma has a high selectivity to etch the amorphous phase relative to the crystalline phase of the first source-drain regions and the crystalline phase of the second source-drain regions.
14. The method of claim 11 , wherein applying the plasma is implemented before forming the two second recesses and after forming the first source-drain regions.
15. The method of claim 11 , wherein applying the plasma is implemented after forming the second source-drain regions.
16. The method of claim 11 , wherein applying the plasma is implemented after each of forming the first source-drain regions and forming the second source-drain regions.
17. The method of claim 9 , wherein the plasma is generated from a gas source including hydrogen.
18. The method of claim 9 ,
wherein the first semiconductor portion is located on a semiconductor substrate;
wherein, after forming the first source-drain regions, each of the first source-drain regions has an outermost sacrificial layer which includes a first region distal from the semiconductor substrate, and a second region proximate to the semiconductor substrate; and
wherein, after applying the plasma, a thickness of the first region is smaller than a thickness of the second region.
19. A semiconductor structure comprising:
a semiconductor substrate; and
a semiconductor portion formed on the semiconductor substrate, and having a channel region and two source-drain regions at two opposite sides of the channel region, each of the source-drain regions having an outermost sacrificial layer, the outermost sacrificial layer including a first region, and a second region, a thickness of the first region being smaller than a thickness of the second region,
wherein the first region is orientated to face away from the semiconductor substrate, and the second region is orientated to face toward the semiconductor substrate; and
wherein the first region and the second region are interconnected to each other at a corner.
20. The semiconductor structure of claim 19 , wherein each of the source-drain regions has a diamond-like shape structure with the corner which is rounded.