Fiber body manufacturing method and fiber body manufacturing apparatus
A fiber body manufacturing method includes: a dispersing step of dispersing a mixture containing a defibrated material which includes fibers and a binding agent which exhibits a binding property by moisture absorption, the mixture having a moisture content of 10 to 30 percent by weight; a depositing step of depositing the mixture dispersed in the dispersing step; a humidifying step of imparting moisture by water vapor or mist to the binding agent in a deposit deposited in the depositing step so as to exhibit the binding property; and a forming step of forming the deposit humidified in the humidifying step into a fiber body.
1. A fiber body manufacturing method comprising:
performing preliminary humidification by humidifying a mixture such that the mixture has a moisture content of 10 to 30 percent by weight, the mixture containing a defibrated material which includes fibers and a binding agent which exhibits a binding property by moisture absorption;
sieving the mixture having the moisture content of 10 to 30 percent by weight, after the performing of the preliminary humidification;
depositing, to obtain a deposit, the mixture that has been sieved;
humidifying the deposit by imparting moisture by water vapor or mist to the binding agent in the deposit so as to exhibit the binding property, the humidifying being performed such that the deposit that has been humidified has a moisture content of 15 to 50 percent by weight; and
forming the deposit that has been humidified into a fiber body.
2. The fiber body manufacturing method according to claim 1 ,
wherein in the preliminary humidification, the mixture is humidified by supply of water vapor or mist.
3. The fiber body manufacturing method according to claim 1 ,
wherein in the sieving, a moisture content of the fibers and a moisture content of the binding agent are each 50 percent by weight or less.
4. The fiber body manufacturing method according to claim 1 ,
wherein the defibrated material is obtained by coarsely pulverizing a raw material including the fibers, followed by performing defibration, and
the preliminary humidification is performed before the raw material is defibrated.
5. The fiber body manufacturing method according to claim 4 ,
wherein the raw material contains the binding agent, and
a content of the binding agent in the raw material is 1 to 50 percent by weight.
6. The fiber body manufacturing method according to claim 1 ,
wherein a content of the binding agent in the fiber body formed in the forming is 1 to 25 percent by weight.