Luminescent component

1. A luminescent component, comprising a first element and a second element, wherein:

said first element comprises a first solid polymer composition, said first polymer composition comprising first luminescent crystals embedded in a first polymer (P 1 ), wherein

said first luminescent crystals are of the perovskite crystal structure and emit light of a first wavelength in response to excitation by light with a wavelength shorter than the first wavelength,

said first polymer (P 1 ) is selected from the group consisting of crosslinked polymers and polymers with Tg<95° C.;

said second element comprises a second solid polymer composition, said second polymer composition optionally comprising second luminescent crystals embedded in a second polymer (P 2 ), wherein

said optional second luminescent crystals are different from said first luminescent crystals and emit light of a second wavelength in response to excitation by light with a wavelength shorter than the second wavelength,

said second polymer (P 2 ) is selected from the group of crosslinked polymers; and wherein

said second element at least partially covers and thereby seals said first element; and

said Tg is measured according to DIN EN ISO 11357-2: 2014-07 during the second heating cycle and applying a heating rate of 20K/min, starting at −90° C. up to 250° C.

2. The luminescent component according to claim 1 , wherein P 1 and/or P 2 complies with one or more of the following parameters:

P 1 has a molar ratio of the sum of (oxygen+nitrogen+sulphur+phosphorous+fluorine+chlorine+bromine+iodine) to carbon <0.9;

P 2 has a molar ratio of the sum of (oxygen+nitrogen+sulphur+phosphorous+fluorine+chlorine+bromine+iodine) to carbon <0.9;

Water vapour transmission rate (WVTR) of P 1 <1 (g*mm)/(m 2 *day);

WVTR of P 2 <1 (g*mm)/(m 2 *day);

Oxygen transmission rate (OTR) of P 1 >1 (cm3*mm)/(m2*day*atm);

OTR of P 2 <50 (cm 3 *mm)/(m 2 *day*atm);

Tg of P 2 >115° C.;

light transmittance of P 1 and P 2 >70%;

wherein the first polymer (P 1 ) is not dissolvable in the second polymer (P 2 ), and vice versa.

3. The luminescent component according to claim 1 , wherein the first polymer (P 1 ) is selected from the group of acrylate polymers and wherein the second polymer (P 2 ) is selected from the group of acrylate polymers.

4. The luminescent component according to claim 1 , wherein the first polymer (P 1 ) comprises repeating units of formulae (III) and (V) and/or the second polymer (P 2 ) comprises repeating units of formula (VI) and optionally of formula (III):

wherein:

R 9 represents H or CH 3 ,

R 10 represents a cyclic, linear or branched C 1-25 alkyl, or a C 6-26 aryl group, each optionally substituted with one or more cyclic, linear or branched C 1-20 alkyl, phenyl or phenoxy,

n represents 0 or 1, and

X represents a spacer from the group of alkoxylates comprising 1-8 carbon atoms and 1-4 oxygen atoms;

wherein:

R 21 independently from each other represent H or CH 3 ;

R 23 represents a cyclic, linear or branched C 1-25 alkyl, or a C 6-26 aryl group, each optionally substituted with one or more cyclic, linear or branched C 1-20 alkyl, phenyl or phenoxy;

X 22 independently from each other represent a spacer selected from the group of alkoxylates, whereby both substituents X 22 together comprise 8-40 carbon atoms and 2-20 oxygen atoms;

wherein:

R 31 independently from each other represent H or CH 3 ;

R 33 represents a cyclic C 5-25 alkyl, or a C 6-26 aryl group, each optionally substituted with one or more cyclic, linear or branched C 1-20 alkyl, phenyl or phenoxy;

X 32 are independent from each other and are either not present or represent a spacer from the group of alkoxylates, whereby both substituents X 32 together comprise 1-8 carbon atoms and 1-8 oxygen atoms.

5. The luminescent component according to claim 1 , wherein the first luminescent crystals are selected from compounds of formula (I):

[M 1 A 1 ] a M 2 b X c   (1), wherein:

A 1 represents one or more organic cations,

M 1 represents one or more alkaline metals,

M 2 represents one or more metals other than M 1 ,

X represents one or more anions selected from the group consisting of halides, pseudohalides and sulfide,

a represents 1-4,

b represents 1-2,

c represents 3-9, and

wherein either M 1 , or A 1 , or M 1 and A 1 being present;

and/or

wherein said first luminescent crystals are of size between 3-100 nm.

6. The luminescent component according to claim 1 , wherein the second luminescent crystals are selected from one or more of core-shell QDs and micron-sized phosphors.

7. The luminescent component according to claim 1 , further comprising third luminescent crystals selected from one or more of perovskite crystals, core-shell QDs and micron-sized phosphors.

8. The luminescent component according to claim 1 in the form of a film, particularly a QD backlight film or a down conversion film, said film comprising the following layered structure:

layer of first element—layer of second element; or

layer of second element—layer of first element—layer of second element; or

protecting layer—layer of second element—layer of first element—layer of second element—protecting layer.

9. The luminescent component according to claim 8 wherein said protecting layer is selected from

glass;

a polymer with humidity barrier properties;

a polymer with oxygen barrier properties; and

a polymer coated with an oxide layer.

10. The luminescent component according to claim 1 , wherein

one or more first elements are arranged on a substrate and covered by a layer comprising said second element; or

a layer comprising said first element is arranged on a substrate and coated by a layer comprising said second element.

11. The luminescent component according to claim 1 , wherein

a plurality of first elements are dispersed in a matrix and fully covered by the second element.

12. A light emitting device, comprising

a luminescent component according to claim 1 ,

a light source for emitting blue light,

wherein the light source is arranged for exciting the luminescent component.

13. The light emitting device according to claim 12 selected from the group consisting of

displays, particularly liquid crystal displays, OLED displays, QLED displays, micro LED displays; and

lighting devices, particularly LEDs, OLEDs, QLEDs.

14. A backlight in a liquid crystal display comprising a luminescent component of claim 1 , for emitting white light in response to the luminescent component being radiated by blue light.

15. A method for manufacturing a luminescent component according to claim 1 , comprising the steps of:

—Method A—

providing a substrate which is optionally coated with one or more layers;

applying to said substrate a first liquid polymer composition comprising monomers or oligomers of the first polymer P 1 , first luminescent crystals, optionally solvent, optionally further materials, optionally third luminescent crystals;

optionally heating said liquid first polymer composition at elevated temperature to remove volatile solvents;

curing said first liquid polymer composition to obtain the first element;

applying to the thus obtained hardened surface of said first element a second liquid polymer composition comprising monomers or oligomers of the second polymer P 2 , optionally second luminescent crystals, optionally solvent, optionally further materials;

optionally heating said liquid second polymer composition at elevated temperature to remove volatile solvents;

curing said liquid second polymer composition to obtain the second element, which covers and thereby seals said first element;

optionally applying further coating or finishing steps; OR

—Method B—

providing a substrate which is optionally coated with one or more layers;

applying to said substrate a second liquid polymer composition as defined above;

optionally heating said liquid second polymer composition at elevated temperature to remove volatile solvents;

curing said second polymer composition to obtain the second element;

applying to the thus obtained hardened surface of said second element a first liquid polymer composition as defined above;

optionally heating said liquid first polymer composition at elevated temperature to remove volatile solvents;

curing said liquid first polymer composition to obtain the first element, which is covered and thereby sealed by said second element on its lower surface;

applying further coating or finishing steps; OR

—Method C—

providing two substrates each coated with a layer of the second element

laminating a layer of first elements with these coated substrates; OR

—Method D—

providing a first liquid polymer composition comprising monomers or oligomers of the first polymer P 1 , first luminescent crystals, optionally solvent, optionally further materials, optionally third luminescent crystals;

one of

a) extracting multiple first elements from the first liquid polymer composition by one of spray-drying, or precipitation, or

b) hardening the first liquid polymer composition into the first solid polymer composition, and crushing the first solid polymer composition resulting in multiple first elements,

mixing the first elements into a second liquid polymer composition as defined above, and

providing a substrate which is optionally coated with one or more layers;

applying to said substrate said second liquid polymer composition containing the first elements;

optionally heating said liquid second polymer composition at elevated temperature to remove volatile solvents;

curing said liquid second polymer composition to obtain the second element, which covers and thereby seals said first elements; and

optionally applying further coating or finishing steps.

16. The luminescent component according to claim 4 in the form of a film, particularly a QD backlight film or a down conversion film, said film comprising the following layered structure:

layer of first element—layer of second element; or

layer of second element—layer of first element—layer of second element; or

protecting layer—layer of second element—layer of first element—layer of second element—protecting layer.