Pure Layered Stretch Film Produced Using Single Pass Extrusion Resins
Methods for producing a stretch film are provided, including disposing one or more extruders in fluid communication with a stock of virgin resin; heating the virgin resin to a molten state; delivering the molten virgin resin to a die; and extruding the molten virgin resin through the die onto a casting roll, thereby creating a cast stretch film. Methods for delivering the molten virgin resin onto a casting roll of varying sizes and set temperatures; and of moving a resulting film onto a secondary chill roll of varying sizes and set temperatures, are also provided. Finally, methods for moving the film from either the casting roll or the secondary chill roll onto a slitting assembly, dividing the film using one more interior or exterior slits, and then capturing and gathering the trim waste but not reintroducing the trim waste back into the production process are also disclosed.
1 . A method for producing a cast stretch film, said method comprising: disposing one or more extruders in fluid communication with a stock of virgin resin; heating said virgin resin to a molten state; delivering said molten virgin resin to a die; and extruding said molten virgin resin through said die onto a casting roll, thereby creating a cast stretch film.
2 . The method of claim 1 , further comprising delivering said molten virgin resin to a die via one or more transfer pipes.
3 . The method claim 1 , further comprising moving said resin from the die onto a matte casting roll.
4 . The method of claim 3 , further comprising moving said resin from the die onto a matte casting roll, wherein said matte casting roll is an approximately 30-inch matte casting roll.
5 . The method of claim 1 , further comprising moving said resin from the die onto a casting roll having a set temperature.
6 . The method of claim 5 , further comprising moving said resin from the die onto a casting roll having a set temperature between about 75° F. and about 100° F.
7 . The method of claim 6 , further comprising moving said resin from the die onto a casting roll having a set temperature of about 90° F.
8 . The method of claim 1 , further comprising moving the film from said casting roll to a secondary chill roll.
9 . The method of claim 8 , further comprising moving the film from said casting roll to a secondary chill roll, wherein said secondary chill roll is an approximately 20-inch chill roll.
10 . The method of claim 8 , further comprising moving the film from said casting roll to a secondary chill roll having a set temperature.
11 . The method of claim of claim 10 , further comprising moving the film from said casting roll to a secondary chill roll having a set temperature between about 65° F. and about 90° F.
12 . The method of claim 11 , further comprising moving the film from said casting roll to a secondary chill roll having a set temperature of about 85° F.
13 . The method of claim 1 , further comprising moving the film from the casting roll onto a slitting assembly.
14 . The method of claim 13 , further comprising using said slitting assembly to form one or more interior slits, thereby creating waste film that is not recycled back into the production process.
15 . The method of claim 13 , further comprising using said slitting assembly to form one or more exterior slits, thereby creating waste film that is not recycled back into the production process.
16 . The method of claim 8 , further comprising moving the film from the secondary chill roll onto a slitting assembly.
17 . The method of claim 16 , further comprising using said slitting assembly to form one or more interior slits, thereby creating waste film that is not recycled back into the production process.
18 . The method of claim 16 , further comprising using said slitting assembly to form one or more exterior slits, thereby creating waste film that is not recycled back into the production process.
19 . The method of claim 1 , further comprising omitting the introduction of any waste material into the virgin resin prior to the melting and extruding processes.
20 . The method of claim 1 , further comprising omitting the introduction of any waste material into the virgin resin during the melting and extruding processes.