Systems and methods for processing fluoropolymer materials and related workpieces
A method for removing perfluorinated compounds from a fluoropolymer material is provided. The method includes the steps of: (a) providing the fluoropolymer material in a chamber; (b) providing an anaerobic environment in the chamber; and (c) providing a fluorination gas in the chamber, thereby exposing the fluoropolymer material to the fluorination gas. The method results in the removal the perfluorinated compounds from the fluoropolymer material.
1. A method of removing perfluorinated compounds, the method comprising the steps of:
(a) providing a fluoropolymer material in a chamber;
(b) heating the chamber to a temperature in a range of 25° C. to 325° C.;
(c) providing an anaerobic environment in the chamber; and
(d) providing a fluorination gas in the chamber after step (c), thereby exposing the fluoropolymer material to the fluorination gas to produce a processed fluoropolymer material,
wherein the fluoropolymer material is in the form of pellets or powders,
wherein an amount of the perfluorinated compounds in the processed fluoropolymer material is less than 300 ppb,
wherein the perfluorinated compounds comprise perfluorooctanoic acid (PFOA) and an amount of the PFOA in the processed fluoropolymer material is less than 1.1 wt. % the amount of the PFOA in the fluoropolymer material, and
wherein the fluoropolymer material is a recycled fluoropolymer material.
2. The method of claim 1 , wherein the fluoropolymer material comprises the perfluorinated compounds used in the manufacture of the fluoropolymer material.
3. The method of claim 1 , wherein the fluoropolymer material is a fluoropolymer micropowder and the amount of PFOA in the processed fluoropolymer material is less than 100 ppt.
4. The method of claim 1 , wherein the fluoropolymer material is a polytetrafluoroethylene (PTFE) micropowder, and the amount of PFOA in the processed fluoropolymer material is less than 100 ppt.
5. The method of claim 1 , wherein the fluoropolymer material is exposed to the fluorination gas at a chamber pressure in a range of 5 psia to 55 psia.
6. The method of claim 1 , wherein the fluoropolymer material is exposed to the fluorination gas for a time period in a range of 1 hour to 1000 hours, and wherein the fluorination gas comprises 1 vol % to 100 vol % fluorine.
7. The method of claim 6 , wherein an amount of the fluorine exposed to the fluoropolymer material ranges from 0.1 pounds of fluorine per 1000 pounds of the fluoropolymer material to 20.0 pounds of fluorine per 1000 pounds of the fluoropolymer material.
8. The method of claim 1 , wherein providing the fluorination gas of step (d) includes providing a continuous flow of the fluorination gas into and/or out of the chamber.
9. The method of claim 1 , wherein the processed fluoropolymer material comprises less than 100 ppb perfluorinated compounds.
10. The method of claim 1 , wherein the processed fluoropolymer material comprises less than 50 ppb perfluorinated compounds.
11. A method for removing perfluorinated compounds, the method comprising the steps of:
(a) providing a fluoropolymer material in a chamber;
(b) providing an anaerobic environment in the chamber;
(c) heating the chamber to a temperature in a range of 25° C. to 325° C.;
(d) providing a fluorination gas in the chamber after step (b), thereby exposing the fluoropolymer material to the fluorination gas to produce a processed fluoropolymer material;
(e) withdrawing the fluorination gas from the chamber; and
(f) withdrawing the processed fluoropolymer material from the chamber,
wherein the fluoropolymer material is in the form of pellets or powders,
wherein the fluoropolymer material comprises the perfluorinated compounds used in the manufacture of the fluoropolymer material,
wherein the perfluorinated compounds comprise perfluorooctanoic acid (PFOA),
wherein an amount of the PFOA in the processed fluoropolymer material is less than 1.1 wt. % the amount of the PFOA in the fluoropolymer material, and
wherein the fluoropolymer material is a recycled fluoropolymer material.
12. The method of claim 11 , the temperature is in the range of 50° C. to 200° C., and wherein the fluoropolymer material is exposed to the fluorination gas for a time period in a range of 1 hour to 48 hours.
13. The method of claim 11 , wherein the processed fluoropolymer material comprises less than 50 ppb perfluorinated compounds.
14. A method for removing perfluorinated compounds, the method comprising the steps of:
(a) providing a fluoropolymer material in a chamber;
(b) providing an anaerobic environment in the chamber;
(c) providing a fluorination gas in the chamber after step (b), thereby exposing the fluoropolymer material to the fluorination gas to produce a processed fluoropolymer material;
(d) withdrawing the fluorination gas from the chamber; and
(e) withdrawing the processed fluoropolymer from the chamber,
wherein the fluoropolymer material comprises the perfluorinated compounds used in the manufacture of the fluoropolymer,
wherein the fluoropolymer material is provided as part of a workpiece,
wherein an amount of the perfluorinated compounds in the processed fluoropolymer material is less than 300 ppb,
wherein the perfluorinated compounds comprise perfluorooctanoic acid (PFOA) and an amount of the PFOA in the processed fluoropolymer material is less than 1.1 wt. % the amount of the PFOA in the fluoropolymer material.
15. The method of claim 14 , further comprising a step of heating the chamber to a temperature in a range of 50° C. to 200° C., and wherein the fluoropolymer material is exposed to the fluorination gas for a time period in a range of 1 hour to 48 hours.
16. The method of claim 14 , wherein the processed fluoropolymer material comprises less than 50 ppb perfluorinated compounds.