Methods of packaging thin metal films to maintain their physical characteristics
The present disclosure is directed to the packaging of metal thin films deposited on polymeric substrates. The packaging method prevents deleterious change of surface energy/water contact angle as a function of time for metal thin films such as rolls, coils, sheets or strips of sputtered or vacuum deposited metal thin films. Methods and kits directed toward a unique packaging and storage scheme are also disclosed. This results in maintenance of the metal film's hydrophilicity and surface energy for extended periods of time.
1. A package, the package comprising:
a roll formed from a metal-coated substrate consisting of a polymeric substrate and a palladium metal coating formed on the polymeric substrate;
a first disc separator and a second disc separator, wherein the first and second disc separators are disposed on opposite sides of the roll, and wherein the first and second disc separators each have a metalized polyester surface contacting the roll; and
a polyester film wrapped around the roll and the first and second disc separators.
2. The package of claim 1 , wherein a surface of the metal coating is hydrophilic in nature.
3. The package of claim 1 , wherein the metal coating has a water contact angle of 55 degrees or less after being wrapped in the polyester film for no less than 24 hours.
4. The package of claim 1 , wherein the metal coating shows, after no less than 58 weeks, at least one of no degradation of surface wettability, no surface fouling, or no loss in surface energy.
5. The package of claim 1 , wherein the metal coating is a thin film formed on the polymeric substrate.
6. The package of claim 5 , wherein the thin film is formed through vacuum deposition.
7. The package of claim 1 , further comprising another covering material wrapped around the polyester film which is wrapped around the roll and the first and second disc separators, thereby forming two wrapping layers.
8. A package, the package comprising:
metal-coated products each comprising a roll, the roll including a polymeric substrate and a palladium metal coating formed on the polymeric substrate;
a first disc separator and a second disc separator, wherein the first and second disc separators are disposed on opposite sides of the roll, wherein the first and second disc separators each have a metalized polyester surface contacting the roll; and
a material covering the metal-coated products and the first and second disc separators, the material selected from a group consisting of a polyester, a metalized polyester, an aluminum foil, and metalized polyethylene terephthalate (PET).
9. The package of claim 8 , wherein a surface of the metal coating is hydrophilic in nature.
10. The package of claim 9 , wherein the metal coating has a water contact angle of 65 degrees or less after being wrapped in the material for no less than 24 hours.
11. The package of claim 8 , wherein the metal coating shows, after no less than 58 weeks, at least one of no degradation of surface wettability, no surface fouling, or no loss in surface energy.
12. The package of claim 8 , wherein the metal coating is a thin film formed on each of the products.
13. The package of claim 12 , wherein the thin film is formed through vacuum deposition.
14. A package, the package comprising:
a roll formed from a metal-coated substrate consisting of a polymeric substrate and a palladium metal coating formed on the polymeric substrate;
a first disc separator and a second disc separator, wherein the first and second disc separators are disposed on opposite sides of the roll, wherein the first and second disc separators each have a metalized polyester surface contacting the roll;
a core, wherein the roll and the first and second disc separators are mounted on the core;
a metal channel, wherein the core is mounted on the metal channel; and
a polyester film wrapped around the roll and the first and second disc separators.
15. The package of claim 14 , wherein a surface of the metal coating is hydrophilic in nature.
16. The package of claim 14 , wherein the metal coating has a water contact angle of 65 degrees or less after being wrapped in the polyester film for no less than 24 hours.
17. The package of claim 14 , wherein the metal coating shows, after no less than 58 weeks, at least one of no degradation of surface wettability, no surface fouling, or no loss in surface energy.
18. The package of claim 14 , wherein the metal coating is a thin film formed on the polymeric substrate.
19. The package of claim 18 , wherein the thin film is formed through vacuum deposition.
20. The package of claim 14 , further comprising another covering material wrapped around the polyester film which is wrapped around the roll and the first and second disc separators, thereby forming two wrapping layers.