Cathode active material for rechargeable lithium battery comprising coating layer comprising lithium fluoride and metal fluoride and method for manufacturing the same
Provided is a positive active material for a rechargeable lithium battery including a nickel-based composite oxide having a nickel content of greater than or equal to 60 mol % relative to a total amount of metal excluding lithium and a coating layer on the surface of the nickel-based composite oxide, wherein the coating layer includes lithium fluoride (LiF) and metal fluoride produced by firing a metal oxide and a fluorine-based organic material.
1. A positive active material for a rechargeable lithium battery, comprising
a nickel-based composite oxide having a nickel content of greater than or equal to 60 mol % relative to a total amount of metal excluding lithium and a coating layer on the surface of the nickel-based composite oxide,
wherein the coating layer comprises:
lithium fluoride (LiF) produced through a reaction of residual lithium of the nickel-based composite oxide with fluorine of a fluorine-based organic material; and
a metal fluoride produced by firing a metal oxide and the fluorine-based organic material, and
wherein the lithium fluoride and metal fluoride are present in a form of nano-sized particulates having a size of greater than or equal to 5 nm and less than or equal to 40 nm.
2. The positive active material of claim 1 , wherein the nickel-based composite oxide is a metal composite oxide represented by Chemical Formula 1:
Li a (Ni 1-x-y-z Co x Mn y M z )O 2 [Chemical Formula 1]
wherein, in Chemical Formula 1, M is an element selected from boron (B), magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), titanium (Ti), vanadium (V), chromium (Cr), iron (Fe), copper (Cu), zirconium (Zr), and aluminum (Al),
0.95≤a≤1.3, x≤(1-x-y-z), y≤(1-x-y-z), 0<x<1, 0≤y<1, and 0≤z<1.
3. The positive active material of claim 1 , wherein the coating layer has a thickness of 20 nm to 70 nm.
4. The positive active material of claim 1 , wherein the coating layer comprises 10 wt % to 90 wt % of the lithium fluoride and 10 wt % to 90 wt % of the metal fluoride.
5. The positive active material of claim 1 , wherein the metal oxide is an oxide including an element selected from a transition metal other than nickel, a Group 13 element capable of reacting with fluorine, and a Group 14 element capable of reacting with fluorine.
6. The positive active material of claim 1 , wherein the metal oxide is selected from aluminum oxide, titanium oxide, zirconium oxide, and a combination thereof.
7. The positive active material of claim 1 , wherein the fluorine-based organic material is a polymer having a melting point of 150° C. to 400° C.
8. The positive active material of claim 1 , wherein the fluorine-based organic material is a polymer or a mixture thereof prepared by polymerizing at least one monomer selected from vinylidene fluoride, tetrafluoroethylene, hexafluoropropylene, chlorotrifluoroethylene, vinyl fluoride, trifluoroethylene, hexafluoroisobutylene, perfluorobutylethylene, perfluoropropyl vinyl ether, perfluoroethyl vinyl ether, perfluoromethyl vinyl ether, perfluoro-2,2-dimethyl-1,3-dioxole, and perfluoro-2-methylene-4-methyl-1,3-dioxolane.
9. The positive active material of claim 1 , wherein the coating layer further comprises the metal oxide.
10. The positive active material of claim 1 , wherein the nickel-based composite oxide comprises a secondary particle in which a plurality of primary particles are agglomerated, wherein the secondary particle has a predetermined arrangement structure in which (003) planes of primary particles are aligned to be in a vertical direction with respect to a tangent line at a point (P) at which the (003) planes of the primary particles meet a surface of the secondary particle.
11. The positive active material of claim 10 , wherein 50% or more of the primary particles are arranged to be in a vertical direction with respect to the tangent line at the point (P) at which the (003) planes meets the surface of the secondary particle.
12. The positive active material of claim 10 , wherein a length in the c-axis direction of the primary particles is in the range of 100 nm to 200 nm.
13. The positive active material of claim 10 , wherein the secondary particle has a radial array structure having one center or a multi-core radial array structure having a plurality of centers.
14. The positive active material of claim 10 , wherein a pore volume fraction of micropores of less than or equal to 10 nm of the secondary particle is greater than or equal to 10% of a total pore volume.
15. A method of preparing the positive active material for a rechargeable lithium battery, comprising
heat-treating a mixture of a metal oxide and a fluorine-based organic material in an oxidizing atmosphere at a temperature of greater than or equal to 350° C. and less than or equal to 650° C., which is equal to or higher than the melting point of the fluorine-based organic material in the presence of the nickel-based composite oxide having a nickel content of greater than or equal to 60 mol % relative to a total amount of metal excluding lithium to prepare the positive active material for a rechargeable lithium battery of claim 1 .
16. The method of claim 15 , wherein the metal oxide and the fluorine-based organic material are mixed in a weight ratio of 30:70 to 70:30 and then fired.