Carbon nanotube dispersion and use thereof
A carbon nanotube dispersion including a carbon nanotube, a solvent, and a dispersant. A highly conductive electrode membrane can be produced as a result of the carbon nanotube using a carbon nanotube dispersion satisfying (1), (2), and (3). (1) An average outer diameter is more than 3 nm and less than 10 nm. (2) A peak is present in a powder X-ray diffraction analysis at a diffraction angle of 2θ=25°±2°, and a half value width of the peak is 3° to 6°. (3) When a maximum peak intensity within the range of 1,560 to 1,600 cm −1 in a Raman spectrum is G and a maximum peak intensity within the range of 1,310 to 1,350 cm −1 is D, a G/D ratio is 0.5 to 4.5.
1. A carbon nanotube dispersion, comprising:
a carbon nanotube;
a solvent; and
a dispersant,
wherein the carbon nanotube satisfies the following (1), (2), and (3):
(1) an average outer diameter is more than 3 nm and less than 10 nm,
(2) a peak appears at a diffraction angle 2θ=25°±2° in powder X-ray diffraction analysis, and a half value width of the peak is 3° to 6°, and
(3) a G/D ratio is 0.5 to 4.5, where G represents a maximum peak intensity in a range of 1,560 to 1,600 cm −1 , and D represents a maximum peak intensity in a range of 1,310 to 1,350 cm −1 in a Raman spectrum.
2. The carbon nanotube dispersion according to claim 1 , wherein a standard deviation of an outer diameter of the carbon nanotube is more than 0.7 nm and equal to or less than 3.5 nm.
3. The carbon nanotube dispersion according to claim 2 , wherein a volume resistivity of the carbon nanotube is 1.0×10 −2 to 2.5×10 −2 Ω·cm.
4. The carbon nanotube dispersion according to claim 3 , wherein the G/D ratio is 1.0 to 3.0.
5. The carbon nanotube dispersion according to claim 2 , wherein the G/D ratio is 1.0 to 3.0.
6. The carbon nanotube dispersion according to claim 2 , wherein the solvent is an amide-based organic solvent or water.
7. The carbon nanotube dispersion according to claim 2 , wherein 5.0 nm≤X±σ≤14.0 nm is satisfied, where X represents the average outer diameter of the carbon nanotube, and σ represents the standard deviation of the outer diameter of the carbon nanotube.
8. The carbon nanotube dispersion according to claim 1 , wherein a volume resistivity of the carbon nanotube is 1.0×10 −2 to 2.5×10 −2 Ω·cm.
9. The carbon nanotube dispersion according to claim 8 , wherein the G/D ratio is 1.0 to 3.0.
10. The carbon nanotube dispersion according to claim 8 , wherein the solvent is an amide-based organic solvent or water.
11. The carbon nanotube dispersion according to claim 8 , wherein 5.0 nm≤X±σ≤14.0 nm is satisfied, where X represents the average outer diameter of the carbon nanotube, and σ represents the standard deviation of the outer diameter of the carbon nanotube.
12. The carbon nanotube dispersion according to claim 1 , wherein the G/D ratio is 1.0 to 3.0.
13. The carbon nanotube dispersion according to claim 12 , wherein the solvent is an amide-based organic solvent or water.
14. The carbon nanotube dispersion according to claim 12 , wherein 5.0 nm≤X±σ≤14.0 nm is satisfied, where X represents the average outer diameter of the carbon nanotube, and σ represents the standard deviation of the outer diameter of the carbon nanotube.
15. The carbon nanotube dispersion according to claim 1 , wherein the solvent is an amide-based organic solvent or water.
16. The carbon nanotube dispersion according to claim 15 , wherein 5.0 nm≤X±σ≤14.0 nm is satisfied, where X represents the average outer diameter of the carbon nanotube, and σ represents the standard deviation of the outer diameter of the carbon nanotube.
17. The carbon nanotube dispersion according to claim 1 , wherein 5.0 nm≤X±σ≤14.0 nm is satisfied, where X represents the average outer diameter of the carbon nanotube, and σ represents the standard deviation of the outer diameter of the carbon nanotube.
18. A carbon nanotube resin composition, comprising:
the carbon nanotube dispersion according to claim 1 ; and
a binder.
19. A composite material slurry, comprising:
the carbon nanotube resin composition according to claim 18 ; and
an active material.
20. An electrode membrane which is coated with the composite material slurry according to claim 19 .