Martensitic stainless steel strip and method for producing same
A martensitic stainless steel strip capable of achieving higher fatigue strength. This martensitic stainless steel strip has a martensite structure and has a thickness of 1 mm or less, and is characterized in that the compressive residual stress at a surface of the steel strip is 50 MPa or more and the areal ratio of carbides present in the metal structure of the steel strip is 0.5-8.0%. The compressive residual stress at a surface of the steel strip is preferably such that the compressive residual stress in a direction perpendicular to rolling is at least 50 MPa greater than the compressive residual stress in the direction of rolling.
1. A martensitic stainless steel strip having a martensite structure and a thickness of 1 mm or smaller,
wherein compressive residual stress on a surface of the martensitic stainless steel strip is 50 MPa or greater, and compressive residual stress in a direction perpendicular to rolling is greater than compressive residual stress in a direction of rolling by 50 MPa or greater, and
wherein an area ratio of carbides present in a metal structure of the martensitic stainless steel strip is 0.5% or more and 8.0% or less.
2. The martensitic stainless steel strip according to claim 1 ,
wherein when carbides having an equivalent circle diameter of 0.10 μm or larger is 100%, the carbides having an equivalent circle diameter within a range of 0.10 μm to 0.50 μm is 45% or more.
3. A method for producing a martensitic stainless steel strip comprising:
an unwinding step of unwinding a martensitic stainless steel strip having a thickness of 1 mm or smaller;
a quenching step of threading and heating the steel strip in a quenching furnace with a non-oxidizing gas atmosphere and subsequently performing cooling; and
a tempering step of threading and tempering the steel strip after the quenching step in a tempering furnace with a non-oxidizing gas atmosphere,
wherein the quenching furnace at a time of the quenching step has at least a temperature raising part and a holding part; when a predetermined quenching temperature is T° C., the temperature raising part is set within a temperature range of 0.7 T° C. or higher and lower than T° C.; a set heating temperature on an output side of the steel strip is set to be higher than a set heating temperature on an input side of the steel strip when the steel strip is threaded the temperature raising part; the holding part is set to the quenching temperature T° C.; and an in-furnace staying time of the steel strip at the temperature raising part is equal to or longer than an in-furnace staying time of the steel strip at the holding part,
wherein the method for producing a martensitic stainless steel strip further comprises a polishing step of polishing a surface of the steel strip after the tempering step through machining,
the martensitic stainless steel strip has a martensite structure and a thickness of 1 mm or smaller,
compressive residual stress on a surface of the martensitic stainless steel strip is 50 MPa or greater, and compressive residual stress in a direction perpendicular to rolling is greater than compressive residual stress in a direction of rolling by 50 MPa or greater, and
an area ratio of carbides present in a metal structure of the martensitic stainless steel strip is 0.5% or more and 8.0% or less.
4. The method for producing a martensitic stainless steel strip according to claim 3 ,
wherein when the in-furnace staying time of the steel strip at the temperature raising part is TS and the in-furnace staying time of the steel strip at the holding part is TH during the quenching step, TS/TH is greater than 1 and smaller than 5.