IRON-BASED SINTERED SLIDING MATERIAL AND METHOD FOR PRODUCING THE SAME
It is possible to provide an iron-based sintered sliding material excellent in the sliding performance. Provided is an iron-based sintered sliding material including, a base containing, by mass, 3 to 15% of S, 0.2 to 6% in a total amount of at least one selected from the group consisting of Cr, Ca, V, Ti, and Mg, and a remainder of Fe and inevitable impurities, sulfide particles containing at least one selected from the group consisting of Cr, Ca, V, Ti, and Mg being dispersed in the base, and pores.
1 . An iron-based sintered sliding material, comprising:
a base containing, by mass, 3 to 15% of S, 0.2 to 6% in a total amount of at least one selected from the group consisting of Cr, Ca, V, Ti, and Mg, and a remainder of Fe and inevitable impurities, sulfide particles containing at least one selected from the group consisting of Cr, Ca, V, Ti, and Mg being dispersed in the base; and
pores.
2 . The iron-based sintered sliding material according to claim 1 , wherein the base further contains 0 to 10% of Ni.
3 . The iron-based sintered sliding material according to claim 1 , wherein the base further contains 0 to 10% of Mo.
4 . The iron-based sintered sliding material according to claim 1 , wherein the base further contains 0 to 1% of graphite.
5 . A sliding part, wherein the iron-based sintered sliding material according to claim 1 is used.
6 . A method for producing an iron-based sintered sliding material, according to claim 1 , comprising:
adding a sulfur alloy powder B to an iron alloy powder A containing not less than 1% by mass in a total amount of at least one selected from the group consisting of Cr, Ca, V, Ti, and Mg such that an amount of sulfur accounts for 3 to 15% by mass of a final sintered compact;
compressing and compacting a mixed powder obtained through the adding; and
sintering a green compact obtained through the compressing and compacting at a temperature in a range from 900° C. to 1,200° C.
7 . The method for producing an iron-based sintered sliding material according to claim 6 , wherein the mixed powder further comprises not less than 3% by mass of at least one selected from the group consisting of a nickel powder and a nickel-iron alloy powder.
8 . The method for producing an iron-based sintered sliding material according to claim 6 , wherein the mixed powder further comprises 0 to 1% by mass of graphite.
9 . An iron-based sintered sliding material, comprising:
a metal sulfide having not less than 20% of an area ratio, wherein
a number of particles of the metal sulfide is not less than 8.0×10 10 particles/m 2 per unit area.
10 . The iron-based sintered sliding material according to claim 9 , wherein
a number of the particles of the metal sulfide, each particle having a particle size of not more than 1 micrometer, accounts for not less than 40% of a total number of the particles of the metal sulfide.
11 . An iron-based sintered sliding material, comprising:
a metal sulfide having not less than 20% of an area ratio, wherein
a number of the particles of the metal sulfide, each particle having a particle size of not more than 1 micrometer, accounts for not less than 40% of a total number of all of the particles of the metal sulfide.
12 . The iron-based sintered sliding material according to claim 9 , wherein the metal sulfide comprises at least one selected from the group consisting of CrS, CaS, VS, TiS, and MgS.
13 . A sliding part comprising the iron-based sintered sliding material according to claim 9 .
14 . The iron-based sintered sliding material according to claim 10 , wherein the metal sulfide comprises at least one selected from the group consisting of CrS, CaS, VS, TiS, and MgS.
15 . The iron-based sintered sliding material according to claim 11 , wherein the metal sulfide comprises at least one selected from the group consisting of CrS, CaS, VS, TiS, and MgS.
16 . The iron-based sintered sliding material according to claim 1 , wherein the base further contains 0 to 10% of Ni, and 0 to 10% of Mo.
17 . The iron-based sintered sliding material according to claim 1 , wherein the base further contains 0 to 10% of Ni, 0 to 10% of Mo, and 0 to 1% of graphite.
18 . The iron-based sintered sliding material according to claim 1 , wherein the base further contains 0 to 10% of Mo, and 0 to 1% of graphite.
19 . The method for producing an iron-based sintered sliding material according to claim 6 , wherein the mixed powder further comprises not less than 3% by mass of at least one selected from the group consisting of a nickel powder and a nickel-iron allow powder, and 0 to 1% by mass of graphite.