Process for continuous supercritical drying of aerogel particles
Processes for drying gel particles, in particular for producing aerogels, involve providing a suspension containing gel particles and a solvent, introducing the suspension into a column where carbon dioxide flows in countercurrent, and removing dried aerogel particles from the column. The suspension is introduced in the top region of the column and dried aerogel particles are removed in the lower region. Pressure and temperature in the column are set such that the mixture of carbon dioxide and solvent is virtually supercritical or is supercritical. The aerogel particles can be discharged via discharge vessels or continuous decompression. Aerogel particles can be obtained by such a process and the aerogel particles can be used for medical and pharmaceutical applications, as additive or carrier material for additives for foods, as catalyst support, for cosmetic, hygiene, washing and cleaning applications, for production of sensors, for thermal insulation, or as a core material for VIPs.
1 . A continuous process for drying gel particles or for producing aerogels, the process comprising:
(i) providing a suspension comprising gel particles and a solvent,
(ii) introducing the suspension into a column through which carbon dioxide flows in countercurrent, and
(iii) removing dried aerogel particles from the column,
wherein the suspension is introduced in a top region of the column and the dried aerogel particles are removed in a lower region of the column,
wherein the pressure and temperature in the column are set such that the mixture of carbon dioxide and solvent is virtually supercritical or is supercritical,
wherein aerogel particles obtained are removed continuously in a valve-free manner using a capillary, and
wherein the gel particles sediment in countercurrent wherein the column has a column length in which a ratio of drying time/residence time is <1.
2 . The process according to claim 1 , wherein a CO 2 mass flow rate is set such that dried aerogel particles are obtained.
3 . The process according to claim 1 , wherein the gel particles have an average diameter in the range from 20 μm to 1000 μm.
4 . The process according to claim 1 , wherein the gel particles have an average pore diameter in the range from 2 to 100 nm.
5 . The process according to claim 1 , wherein the solvent is selected from the group consisting of methanol, ethanol, propanol, butanol, pentanol and hexanol.
6 . The process according to claim 1 , wherein the column is installed above an intermediate collecting vessel into which the dried aerogel particles fall as a result of gravity, and/or using a fluidization aid to discharge the particles from an intermediate vessel by means of a CO 2 stream to prevent blocking of a capillary inlet.
7 . The process according to claim 6 , wherein the carbon dioxide mass flow rate directly upward countercurrent to a falling direction of the particles is to a ratio of drying time/residence time of <1.