Easily-crushable copper powder and manufacturing method therefor
Provided is a copper powder manufactured by means of a wet method, wherein the absolute value of the zeta potential of the copper powder is at least 20 mV. The copper powder can be manufactured so as to reduce the burden of the steps of crushing a dry cake and classification, and there is a sufficient reduction in residual secondary particles.
1. A method for providing copper powder with easy crushability, the method comprising a pH treatment step comprising bringing copper consisting of copper powder produced by a wet method into contact with an aqueous alkaline solution having a pH of from 8 to 14 or an aqueous acidic solution having a pH of from 0 to 4, wherein said copper powder produced by a wet method has not undergone a form of dried cake after being produced by the wet method and prior to being brought into contact with the aqueous alkaline solution or aqueous acidic solution.
2. A method for manufacturing easily-crushable copper powder, the method comprising a pH treatment step comprising bringing copper consisting of copper powder produced by a wet method into contact with an aqueous alkaline solution having a pH of from 8 to 14 or an aqueous acidic solution having a pH of from 0 to 4, wherein said copper powder produced by a wet method has not undergone a form of dried cake after being produced by the wet method and prior to being brought into contact with the aqueous alkaline solution or aqueous acidic solution.
3. The method according to claim 1 , the copper powder produced by a wet method is in the form of slurry of the copper powder.
4. The method according to the claim 2 , the copper powder produced by a wet method is in the form of slurry of the copper powder.
5. The method according to the claim 1 , after the pH treatment step the method further comprising steps of:
obtaining a copper powder dried cake by washing the copper powder subjected to the pH treatment and then drying the copper powder, and
crushing the copper powder dried cake.
6. The method according to the claim 2 , after the pH treatment step the method further comprising steps of:
obtaining a copper powder dried cake by washing the copper powder subjected to the pH treatment and then drying the copper powder, and
crushing the copper powder dried cake.
7. The method according to the claim 3 , after the pH treatment step the method further comprising steps of:
obtaining a copper powder dried cake by washing the copper powder subjected to the pH treatment and then drying the copper powder, and
crushing the copper powder dried cake.
8. The method according to the claim 4 , after the pH treatment step the method further comprising steps of:
obtaining a copper powder dried cake by washing the copper powder subjected to the pH treatment and then drying the copper powder, and
crushing the copper powder dried cake.