Two-dimensional semiconductor based printable optoelectronic inks, fabricating methods and applications of same
Printable inks based on a 2D semiconductor, such as MoS2, and its applications in fully inkjet-printed optoelectronic devices are disclosed. Specifically, percolating films of MoS2 nanosheets with superlative electrical conductivity (10-2 s m−1) are achieved by tailoring the ink formulation and curing conditions. Based on an ethyl cellulose dispersant, the MoS2 nanosheet ink also offers exceptional viscosity tunability, colloidal stability, and printability on both rigid and flexible substrates. Two distinct classes of photodetectors are fabricated based on the substrate and post-print curing method. While thermal annealing of printed devices on rigid glass substrates leads to a fast photoresponse of 150 μs, photonically annealed devices on flexible polyimide substrates possess high photoresponsivity exceeding 50 mA/W. The photonically annealed photodetector also significantly reduces the curing time down to the millisecond-scale and maintains functionality over 500 bending cycles, thus providing a direct pathway to roll-to-roll manufacturing of next-generation flexible optoelectronics.
1. A method of forming a printable optoelectronic ink, comprising:
providing a composite comprising at least one 2D semiconductor and a binder; and
dispersing the composite in a solvent system,
wherein viscosity of the printable optoelectronic ink is tunable and optimizable by dispersing said composite in the solvent system at different loadings; and
wherein the printable optoelectronic ink is formed to possess a super-linear dependence of the viscosity on mass loading and reduced viscosities at elevated temperatures.
2. The method of claim 1 , wherein the step of providing said composite comprises:
dissolving the binder in a first solvent to form a first mixture, and adding at least one 2D semiconductor in the first mixture to form a second mixture;
shear-mixing the second mixture, and centrifuging the shear-mixed second mixture to sediment out undesired size particles of the at least one 2D semiconductor, so as to form a supernatant containing the remaining size particles of the at least one 2D semiconductor, the binder, and the first solvent;
decanting and flocculating the supernatant by mixing with an aqueous solution to form a third mixture and centrifuging the third mixture to obtain a wet composite of the at least one 2D semiconductor and the binder; and
rinsing the wet composite with deionized water, collecting the rinsed composite by vacuum filtration, and drying the collected composite in air to yield powder of said composite.
3. The method of claim 2 , wherein a content of the at least one 2D semiconductor in said composite is in a range of about 20-70 wt %.
4. The method of claim 1 , wherein the step of dispersing said composite is performed with loadings of about 10-80 mg/mL using bath sonication.
5. The method of claim 1 , wherein the at least one 2D semiconductor comprises nanoparticles comprising nanosheets, nanoflakes, nanofibers, nanotubes, or combinations of them.
6. The method of claim 5 , wherein the at least one 2D semiconductor comprises MoS 2 , WS 2 , ReS 2 , InSe, GaTe, or black phosphorus (BP).
7. The method of claim 1 , wherein the printable optoelectronic ink is formed such that a film is operably formable to have percolating networks by a single printing pass, or multiple printing passes of the printable optoelectronic ink.
8. The method of claim 7 , wherein the binder comprises a polymer stabilizer adapted to achieve high loading and uniform dispersion of the at least one 2D semiconductor in the solvent system.
9. The method of claim 7 , wherein the binder is adapted such that annealing of the film results in decomposition of the binder, thereby forming a percolating film in which electrical contact between the nanoparticles is enhanced.
10. The method of claim 9 , wherein the binder comprises ethyl cellulose (EC), nitrocellulose, cellulose sulfate, methyl cellulose, ethyl methyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, hydoxyethyl methyl cellulose, or carboxymethyl cellulose.
11. The method of claim 1 , wherein the solvent system is a dual solvent system containing cyclohexanone and terpineol.
12. The method of claim 1 , wherein the printable optoelectronic ink is applicable for inkjet printing, spray coating, screen printing, and/or blade coating.