Brazing filler material for bonding iron-based sintered member, and method for producing iron-based sintered part
Provided is a brazing filler material for bonding iron-based sintered member that includes a sintered compact containing Cu, Mn, and a remainder of Ni and unavoidable impurities, and an oxide film formed on a surface of the sintered compact. An oxygen concentration may account for not less than 0.1% by mass of a total amount of the brazing filler material. The oxide film may contain Mn.
1. A brazing filler material for bonding iron-based sintered member, comprising:
a sintered compact containing Cu, Mn, and a remainder of Ni and unavoidable impurities; and
an oxide film formed on a surface of the sintered compact, the oxide film containing MnO,
wherein an oxygen concentration of the brazing filler material accounts for not less than 0.13% by mass of a total amount of the brazing filler material; and
wherein a specific surface area of the brazing filler material is not more than 650 cm 2 /g.
2. A brazing filler material for bonding iron-based sintered member, comprising:
a sintered compact containing Cu, Mn, and a remainder of Ni and unavoidable impurities; and
an oxide film formed on a surface of the sintered compact, the oxide film containing MnO,
wherein an oxygen concentration of the brazing filler material accounts for not less than 0.13% by mass of a total amount of the brazing filler material; and
wherein a mass ratio (A/B) of an amount of oxygen A of a surface layer part of the brazing filler material relative to an amount of oxygen B at a central part of the brazing filler material is not less than 1.
3. The brazing filler material for bonding iron-based sintered member according to claim 2 , wherein a mass ratio (A/B) of an amount of oxygen A of a surface layer part of the brazing filler material relative to an amount of oxygen B at a central part of the brazing filler material exceeds 1.
4. The brazing filler material for bonding iron-based sintered member according to claim 2 , wherein a mass ratio (A/B) of an amount of oxygen A of a surface layer part of the brazing filler material relative to an amount of oxygen B at a central part of the brazing filler material is not less than 1.5.
5. A brazing filler material for bonding iron-based sintered member, comprising:
a sintered compact containing Cu, Mn, and a remainder of Ni and unavoidable impurities; and
an oxide film formed on a surface of the sintered compact, the oxide film containing MnO,
wherein an oxygen concentration of the brazing filler material accounts for 0.15 to 0.2% by mass of a total amount of the brazing filler material.
6. The brazing filler material for bonding iron-based sintered member according to claim 5 , wherein the oxide film containing MnO on the surface of the sintered compact of the brazing filler material is formed in advance before bonding an iron-based sintered member.
7. A method for producing a brazing filler material for bonding iron-based sintered member according to claim 5 , comprising:
preparing a green compact by using a mixed powder blended so as to have a composition of the sintered compact,
preparing the sintered compact by applying a heat treatment to the green compact in a non-oxidizing atmosphere, and
applying an oxidation treatment to the sintered compact by applying a heat treatment to the sintered compact in an oxidizing atmosphere.
8. A method for producing an iron-based sintered part, comprising:
providing the brazing filler material for bonding iron-based sintered member according to claim 5 , and producing an iron-based sintered part comprising a plurality of iron-based sintered members bonded by using the brazing filler material.
9. The method for producing an iron-based sintered part according to claim 8 , wherein the oxide film of the brazing filler material containing MnO on the surface of the sintered compact of the brazing filler material is formed in advance before bonding the iron-based sintered member.