Steel plate for pressure vessel with excellent cryogenic toughness and excellent ductility and manufacturing method thereof
Provided are a steel plate for a pressure vessel with excellent cryogenic toughness and excellent ductility, and a manufacturing method thereof. The steel plate for a pressure vessel of the present invention comprises, in weight %, 0.05 to 0.15% of C; 0.20 to 0.40% of Si; 0.3 to 0.6% of Mn; 0.001 to 0.05% of Al; 0.012% or less of P; 0.015% or less of S; 4.0 to 5.0% of Ni; 0.001 to 0.10% of In; and the balance being Fe and unavoidable impurities, wherein a steel microstructure consists of 15 to 80 area % of tempered bainite and the balance being tempered martensite.
1. A steel plate for a pressure vessel, consisting of:
in weight %, 0.05 to 0.15% of C, 0.20 to 0.40% of Si, 0.3 to 0.6% of Mn, 0.001 to 0.05% of Al, 0.012% or less of P, 0.015% or less of S, 4.0 to 5.0% of Ni, 0.05 to 0.08% of In, a balance of Fe, and unavoidable impurities,
wherein a steel microstructure is comprised of 15 to 80 area % of tempered bainite and a balance tempered martensite.
2. The steel plate for a pressure vessel of claim 1 , wherein the In is contained in a range of 0.07 to 0.08%.