Aqueous exfoliated graphene by amphiphilic cellulose nanofibrils for foldable and moisture-responsive nanopaper
View Patent ↗The present invention describes a method for preparing graphene by mixing graphite and carbon nanofibrils. The prepared graphene can be used to form nanopaper. The present invention also provides a method of preparing nanopaper by suspending cellulose nanofibrils and graphene, followed by vacuum filtering of the suspension.
1. A method for preparing graphene comprising mixing graphite and carbon nanofibrils in a solvent to form a mixture comprising graphene at a concentration of at least 0.01 mg mL −1 , wherein the solvent comprises water.
2. The method of claim 1 , wherein the carbon nanofibrils comprise cellulose nanofibrils.
3. The method of claim 1 , wherein the weight ratio of the graphite to the carbon nanofibrils is from about 0.2:1 to about 33:1, about 0.2:1, 0.5:1, 1:1, 2:1, 3:1, 6:1, 6.6:1, 7:1, 10:1, 15:1, 20:1, or about 33:1.
4. The method of claim 1 , wherein the weight ratio of the graphite to the carbon nanofibrils is from about 1:5 to about 33:1.
5. The method of claim 1 , wherein the combined weight of the graphite and the carbon nanofibrils is from about 0.1% to about 0.4%, about 0.1%, 0.12%, 0.14%, 0.16%, 0.2%, 0.24%, 0.26%, 0.3%, 0.32%, 0.35%, or about 0.4%, of the total weight of the mixture.
6. The method of claim 1 , wherein the mixture comprises graphene at a concentration of at least 0.1 mg mL −1 .
7. The method of claim 1 , wherein the mixture comprises graphene at a concentration of at least 0.5 mg mL −1 .
8. The method of claim 1 , wherein the mixing is performed using a high-speed blender.