Method of producing polyamide fine particles, and polyamide fine particles
A method produces polyamide fine particles by polymerizing a polyamide monomer (A) in the presence of a polymer (B) at a temperature equal to or higher than the crystallization temperature of a polyamide to be obtained, wherein the polyamide monomer (A) and the polymer (B) are homogeneously dissolved at the start of polymerization, and polyamide fine particles are precipitated after the polymerization. Polyamide fine particles have a number average particle size of 0.1 to 100 μm, a sphericity of 90 or more, a particle size distribution index of 3.0 or less, a linseed oil absorption of 100 mL/100 g or less, and a crystallization temperature of 150° C. or more.
1. Polyamide fine particles, wherein polyamide constituting the polyamide fine particles is polyamide 4 or polyamide 3, the polyamide fine particles have a number average particle size of 0.1 to 300 μm, a particle size distribution index of 1.00 to 1.45, a sphericity of 90 or more, and a linseed oil absorption of 100 mL/100 g or less.
2. The polyamide fine particles according to claim 1 , wherein the linseed oil absorption of the polyamide fine particles is 70 mL/100 g or less.
3. The polyamide fine particles according to claim 1 , wherein polyamide constituting the polyamide fine particles is polyamide 4.
4. The polyamide fine particles according to claim 1 , wherein biodegradability of the polyamide fine particles according to JIS K 6955 (2006) is 25 to 70%.
5. The polyamide fine particles according to claim 1 , wherein the weight average molecular weight of the polyamide fine particles is 30,000 to 82,000.
6. The polyamide fine particles according to claim 1 , wherein the sphericity of the polyamide fine particles is 95 or more.
7. The polyamide fine particles according to claim 1 , wherein a theoretical ratio of surface areas R calculated by equation (1) is 5 or less.
R=ADiα/ 6 (1)
Di: number average particle diameter of each particle, α: density of polyamide, and A: BET specific surface area.
8. The polyamide fine particles according to claim 7 , wherein the linseed oil absorption of the polyamide fine particles is 70 mL/100 g or less.
9. The polyamide fine particles according to claim 7 , wherein polyamide constituting the polyamide fine particles is polyamide 4.
10. The polyamide fine particles according to claim 7 , wherein biodegradability of the polyamide fine particles according to JIS K 6955 (2006) is 25 to 70%.
11. The polyamide fine particles according to claim 7 , wherein the weight average molecular weight of the polyamide fine particles is 30,000 to 82,000.
12. The polyamide fine particles according to claim 7 , wherein the sphericity of the polyamide fine particles is 95 or more.