Production of lithium chemicals and metallic lithium
A process and system are disclosed for producing lithium oxide from lithium nitrate. In the process and system, the lithium nitrate is thermally decomposed in a manner such that a fraction of the lithium nitrate forms lithium oxide, and such that a remaining fraction of the lithium nitrate does not decompose to lithium oxide. The thermal decomposition may be terminated after a determined time period to ensure that there is a remaining fraction of lithium nitrate and to thereby produce a lithium oxide in lithium nitrate product. The lithium oxide in lithium nitrate product may have one or more transition-metal oxides, hydroxides, carbonates or nitrates added thereto to form a battery electrode. The lithium oxide in lithium nitrate product may alternatively be subjected to carbothermal reduction to produce lithium metal.
1. A process for producing a mixture of lithium oxide and lithium nitrate from a lithium nitrate starting material, the process comprising:
thermally decomposing at a temperature greater than about 600° C. the lithium nitrate starting material such that a fraction of the lithium nitrate starting material decomposes to lithium oxide and a remaining fraction of the lithium nitrate starting material does not decompose to lithium oxide,
wherein the thermal decomposition is terminated after a determined time period to ensure the remaining fraction of lithium nitrate, thereby forming the mixture of lithium oxide and lithium nitrate, and wherein the fraction of lithium nitrate starting material that is thermally decomposed to lithium oxide is no more than 96% by weight of the lithium nitrate starting material.
2. The process according to claim 1 , wherein terminating the thermal decomposition after the determined time period comprises cooling the mixture to below a decomposition temperature of 600° C.
3. The process according to claim 2 , the process further comprising cooling the mixture of lithium oxide and lithium nitrate to a temperature of less than 260° C., thereby producing a solid mixture of lithium oxide and lithium nitrate.
4. The process according to claim 3 , wherein the solid blend mixture of lithium oxide and lithium nitrate is produced so as to take the form of one or more of: prills, pellets, flakes.
5. The process according to claim 1 , the process further comprising heating the solid mixture of lithium oxide and lithium nitrate so as to form molten lithium nitrate that comprises the lithium oxide dispersed therein, and further comprising adding thereto: a transition-metal oxide, a hydroxide, a carbonate, a nitrate, or any combination thereof.
6. The process according to claim 1 , wherein the lithium nitrate starting material is molten lithium nitrate salt.
7. The process according to claim 1 , wherein the thermal decomposition also produces gases comprising oxygen and oxides of nitrogen, and wherein the process further comprises passing said gases to a nitric acid production stage.
8. The process according to claim 1 , wherein the thermal decomposition also produces gases, and wherein the thermal decomposition comprises direct or indirect heating of the lithium nitrate starting material.
9. The process according to claim 1 , the process further comprising converting the mixture of lithium oxide and lithium nitrate to lithium metal.
10. The process according to claim 1 , wherein the lithium nitrate starting material comprises a salar.
11. The process according to claim 1 , wherein the lithium nitrate starting material is a lithium nitrate solution produced from a salar by a process comprising: taking a lithium-rich brine (LiCl) from a salar-treatment stage and adding a nitrate salt thereto to obtain a resulting mixture, and subjecting the resulting mixture to a thermal treatment stage so as to produce the lithium nitrate solution.
12. The process according to claim 11 , wherein the nitrate salt is Chile saltpetre (NaNO 3 ).
13. The process according to claim 11 , wherein the thermal treatment stage comprises evaporation.
14. A process for producing liquid lithium nitrate with solid lithium oxide therein, from a lithium nitrate starting material, the process comprising:
thermally decomposing the lithium nitrate starting material by heating the lithium nitrate tarting material to a temperature that is 600° C. or greater such that a fraction of the lithium nitrate starting material decomposes to lithium oxide and a remaining fraction of the lithium nitrate starting material does not decompose to lithium oxide, wherein the fraction of lithium nitrate starting material that is thermally decomposed to lithium oxide is no more than 96% by weight of the lithium nitrate starting material, and thereby producing a resulting mixture comprising lithium nitrate and lithium oxide; and
cooling the resulting mixture comprising lithium nitrate and lithium oxide to a temperature that is below 600° C. and that is above the melting temperature of the lithium oxide, thereby obtaining the liquid lithium nitrate with solid lithium oxide therein.
15. The process according to claim 14 ,
wherein said cooling of the resulting mixture comprising lithium nitrate and lithium oxide comprises: cooling the resulting mixture comprising lithium nitrate and lithium oxide to a temperature that is below 600° C. and above 260° C.
16. The process according to claim 15 , the process further comprising: cooling the liquid lithium nitrate with solid lithium oxide therein to a temperature that is under 260° C., thereby producing solid lithium nitrate with solid lithium oxide therein.
17. The process according to any one of claims 14-16 , wherein the fraction of lithium nitrate starting material that is thermally decomposed to lithium oxide is no more than 90% by weight of the lithium nitrate starting material.
18. The process according to any one of claims 14-16 , wherein the fraction of lithium nitrate starting material that is thermally decomposed to lithium oxide is in the range of from 50-90% by weight of the lithium nitrate starting material.
19. The process according to any one of claims 14-16 , wherein the fraction of lithium nitrate starting material that is thermally decomposed to lithium oxide is in the range of from 70-90% by weight of the lithium nitrate starting material.