Thermoplastic Vulcanizate Compositions Comprising Encapsulated Stannous Chloride
Masterbatch compositions comprising encapsulated stannous chloride for use in the production of thermoplastic vulcanizates, and methods related thereto. For example, the present disclosure provides for a composition comprising stannous chloride powder encapsulated in a carrier compound, the carrier compound being solid at a temperature in the range of 15.5° C. to 260° C. (60° F. to 500° F.).
1 . A composition comprising stannous chloride powder encapsulated in a carrier compound, the carrier compound being solid at a temperature in the range of 15.5° C. to 260° C. (60° F. to 500° F.) and selected from the group consisting of an oligomer, a natural wax, an oleochemical, a water-soluble polymer, a non-thermoplastic polymer, and any combination thereof.
2 . The composition of claim 1 , wherein the carrier compound comprises the oligomer, the natural wax, the oleochemical, or a combination thereof.
3 . The composition of claim 1 , wherein the carrier compound has a molecular weight of less than 2000 g/mol.
4 . The composition of claim 1 , wherein the compound is solid at a temperature in the range of 15.5° C. to 27.7° C.
5 . The composition of claim 1 , wherein the carrier compound comprises the oligomer.
6 . The composition of claim 5 , wherein the oligomer has a degree of polymerization in the range of 2 to 100.
7 . The composition of claim 5 , wherein the oligomer is an amorphous, glassy, hydrocarbon oligomer.
8 . The composition of claim 1 , wherein the stannous chloride powder is present in an amount of 0.5% to 99.5% by total weight of the composition.
9 . The composition of claim 1 , wherein the stannous chloride powder is one or more of anhydrous stannous chloride powder and di-hydrated stannous chloride powder.
10 . The composition of claim 1 , further comprising an additive.
11 . The composition of claim 10 , wherein the additive is a filler material.
12 . The composition of claim 11 , wherein the filler material is present in an amount of 0.5% to 85% by total weight of the composition.
13 . The composition of claim 1 , wherein the composition is in the form of one or more of free flowing pellets, granules, flakes, and pastilles.
14 . The composition of claim 13 , wherein the one or more free flowing pellets, granules, flakes, and pastilles have a particle size of from 100 micrometers to 10 millimeters.
15 . A method for producing the composition of claim 1 comprising:
supplying stannous chloride powder and the carrier compound to a mixer;
compounding the stannous chloride powder and the carrier compound in the mixer at a temperature above a melting point of the carrier compound to form a molten mixture; and
cooling the molten mixture to form the composition.
16 . The method of claim 15 , further comprising extruding the molten mixture through a die prior to cooling.
17 . The method of claim 15 , further comprising one or more of pelletizing, granulizing, flaking, and pastillizing the cooled molten mixture.
18 . The method of claim 17 , wherein the one or more pelletized, granulized, flaked, and pastillized cooled molten mixture have a particle size of from 100 micrometers to 10 millimeters.
19 . The method of claim 15 , further comprising supplying a filler material to the mixer with the stannous chloride powder and the carrier compound.
20 . The method of claim 19 , wherein the filler material is clay.
21 . The method of claim 19 , wherein the filler material is present in an amount of 0.5% to 85% by total weight of the composition
22 . The method of claim 15 , wherein the temperature is in the range of from 15.5° C. to 260° C.
23 . A method for producing a thermoplastic vulcanizate (TPV) comprising the composition of claim 1 , the method comprising:
supplying components comprising a rubber component, a thermoplastic component, a curing agent, and the composition to a mixer;
mixing the components at a temperature above a melting point of the thermoplastic component to melt the thermoplastic component and at least partially cross-link the rubber component to produce a heterogeneous product comprising particles of the rubber component dispersed in a matrix of the thermoplastic component.
24 . The method of claim 23 , wherein the curing agent is supplied to the mixer after the rubber component, the thermoplastic component, and the composition.
25 . The method of claim 23 , wherein the thermoplastic component is polypropylene.
26 . The method of claim 23 , wherein the rubber component is ethylene propylene diene terpolymer.
27 . The method of claim 23 , wherein the temperature is in the range of from 15.5° C. to 260° C.
28 . The method of claim 23 , wherein the TPV has a hardness of from 20 Shore A to 60 Shore D.
29 . The method of claim 23 , wherein the TPV has a specific gravity of from 0.8 to 1.4.
30 . The method of claim 23 , wherein the TPV has a 100% Modulus of from 0.5 megapascal to 10 megapascals.
31 . The method of claim 23 , wherein the TPV has a tensile strength at break of from 1 megapascal to 20 megapascals.
32 . The method of claim 23 , wherein the TPV has an elongation at break of from 50% to 1000%.
33 . The method of claim 23 , wherein the TPV has a compression set of from 15% to 80%.