High strength steel sheet having excellent ductility and workability, and method for manufacturing same

1. A steel sheet comprising; by weight %, carbon (C): more than 0.25% to 0.75%, silicon (Si): 4.0% or less, manganese (Mn): 0.9 to 5.0%, aluminum (Al): 5.0% or less, phosphorus (P): 0.15% or less, sulfur (S): 0.03% or less, nitrogen (N): 0.03% or less, and a balance of iron (Fe) and inevitable impurities; anda microstructure comprises, by volume %, 30-75% of tempered martensite, 10 to 50% of bainite, 10 to 40% of retained austenite, 5% or less of ferrite, and an inevitable structure, and satisfying the following Relational Expression 1,

0.55≤[Si+Al]γ/[Si+Al] av≤ 0.85,  [Relational Expression 1]

where [Si+Al]γ is a content (weight %) of Si and Al contained in the retained austenite, and [Si+Al]av is a content (weight %) of Si and Al contained in the high-strength steel sheet,

wherein R/t is 0.5 to 3.0 where R is a minimum bending radius (mm) at which cracking does not occur after a 900 bending test and t is a thickness (mm) of the steel sheet.

2. The high-strength steel sheet of claim 1 , further comprising at least one of (1) to (9):

(1) at least one of titanium (Ti): 0 to 0.5%, niobium (Nb): 0 to 0.5%, and vanadium (V): 0 to 0.5%;

(2) at least one of chromium (Cr): 0 to 3.0% and molybdenum (Mo): 0 to 3.0%;

(3) at least one of copper (Cu): 0 to 4.5% and nickel (Ni): 0 to 4.5%;

(4) boron (B): 0 to 0.005%;

(5) at least one of calcium (Ca): 0 to 0.05%, a rare earth element (REM) except yttrium (Y): 0 to 0.05%, and magnesium (Mg): 0 to 0.05%;

(6) at least one of tungsten (W): 0 to 0.5% and zirconium (Zr): 0 to 0.5%;

(7) at least one of antimony (Sb): 0 to 0.5% and tin (Sn): 0 to 0.5%;

(8) at least one of yttrium (Y): 0 to 0.2% and hafnium (Hf): 0 to 0.2%; and

(9) cobalt (Co): 0 to 1.5%.

3. The high-strength steel sheet of claim 1 , wherein a sum of silicon and aluminum (Si+Al) is 1.0 to 6.0%.

4. The steel sheet of claim 1 , wherein a product of tensile strength and elongation (TS×El) is 22,000 MPa % or more.

5. A method of manufacturing the steel sheet of claim 1 , the method comprising: heating a steel slab and hot rolling the heated steel slab to obtain a hot-rolled steel sheet, the steel slab comprising, by weight %, carbon (C): more than 0.25% to 0.75%, silicon (Si): 4.0% or less, manganese (Mn): 0.9 to 5.0%, aluminum (Al): 5.0% or less, phosphorus (P): 0.15% or less, sulfur (S): 0.03% or less, nitrogen (N): 0.03% or less, and a balance of iron (Fe) and inevitable impurities; coiling the hot-rolled steel sheet; performing a hot-rolling annealing heat treatment on the coiled steel sheet in a temperature range of 650 to 850° C. for 600 to 1700 seconds; cold rolling the coiled steel sheet subjected to the hot-rolling annealing heat treatment; heating the cold-rolled steel sheet to Ac3 or higher (first heating) and holding the first-heated steel sheet for 50 seconds or more (first holding); cooling the first-heated steel sheet to a temperature range of 100 to 300° C. at an average cooling rate of 1° C./sec (first cooling); heating the first-cooled steel sheet to a temperature range of 300 to 500° C. (second heating) and holding the second-heated steel sheet in the temperature range of 300 to 500° C. for 50 seconds or more (second holding); and cooling the second-heated steel sheet to room temperature; thereby producing the steel sheet of claim 1 .

6. The method of claim 5 , wherein the cold-rolled steel sheet further comprises at least one of (1) to (9):

(1) at least one of titanium (Ti): 0 to 0.5%, niobium (Nb): 0 to 0.5%, and vanadium (V): 0 to 0.5%;

(2) at least one of chromium (Cr): 0 to 3.0% and molybdenum (Mo): 0 to 3.0%;

(3) at least one of copper (Cu): 0 to 4.5% and nickel (Ni): 0 to 4.5%;

(4) boron (B): 0 to 0.005%;

(5) at least one of calcium (Ca): 0 to 0.05%, a rare earth element (REM) except yttrium (Y): 0 to 0.05%, and magnesium (Mg): 0 to 0.05%;

(6) at least one of tungsten (W): 0 to 0.5% and zirconium (Zr): 0 to 0.5%;

(7) at least one of antimony (Sb): 0 to 0.5% and tin (Sn): 0 to 0.5%;

(8) at least one of yttrium (Y): 0 to 0.2% and hafnium (Hf): 0 to 0.2%;

(9) cobalt (Co): 0 to 1.5%.

7. The method of claim 5 , wherein the steel slab is heated to a temperature in a range of 1000 to 1350° C., and hot rolling comprises performing finish hot rolling in a temperature range of 800 to 1000° C.

8. The method of claim 5 , wherein the coiling is performed in a temperature range of 300 to 600° C.

9. The method of claim 5 , wherein the cold rolling is performed at a reduction ratio of 30 to 90%.

10. The method of claim 5 , wherein a rate of the second heating is 5° C./sec or more.

11. The method of claim 5 , wherein a rate of the second cooling is 1° C./sec or more.